三聚氰胺甲醛树脂交联剂可明显改善聚合物水泥基涂料的力学性能、耐热性能和耐水性能。
The mechanical properties and the resistance to water and heat of the polymer modified cement based waterproofing coating are greatly improved by the synthesized melamine resin.
在介绍三聚氰胺特点、三聚氰胺甲醛树脂改性、三聚氰胺衍生物合成的基础上，系统介绍相关应用。
The applications of melamine are described systematically on the basis of introducing the characteristics of melamine, the modification of melamine formaldehyde resin and melamine derivatives.
采用三聚氰胺甲醛树脂（MF）作为囊壁，用原位聚合法对生物农药鱼藤酮进行包囊，制备微胶囊制剂。
The preparation of microcapsules of bio-pesticide rotenone by means of in-situ polymerization, with melamine formaldehyde resin(MF) as the shell material, is discussed in this paper.
以三聚氰胺甲醛树脂、磺化三聚氰胺甲醛树脂两种重要中间体的合成为例，分析阐述了三聚氰胺改性合成机理。
The synthesis of melamine-formaldehyde resin and its sulfonate were quoted to illustrate the mechanism of the chemical modification of melamine.
采用苯甲酸改性的醇酸树脂和混合醚化的三聚氰胺甲醛树脂为基料，配以适量的锤纹助剂制成高固体分低温快干型氨基锤纹漆。
The high-solid fast drying amino hammer paint is prepared with benzoic acid modified alkyd resin and etherified melamine-formaldehyde resin as binder, hammering agent and other components.
以改性三聚氰胺甲醛树脂（MF树脂）和酚醛树脂（PF树脂）为胶粘剂，设计了两组热压工艺参数，按照“冷-热-冷”工艺压制竹帘胶合板。
Taking modified MF and PF resin as the adhesive and using "cool-hot-cool" technology, this paper designs two groups of technological parameters of hot-pressing to press bamboo curtain plywood.
含胺基或氨基树脂是尿素或三聚氰胺和甲醛烷基化反应产品。
An amine or amino resin is the alkylated reaction product of urea or melamine and formaldehyde.
人造板工业使用的三大胶是脲醛树脂胶、酚醛树脂胶和三聚氰胺-甲醛树脂胶。
The three main adhesives for artificial plate are urea-formaldehyde resin adhesive, phenolic-formaldehyde resin adhesive and melamine-formaldehyde resin adhensive.
环氧树脂先与三聚氰胺和脲在一定条件下反应，然后再与甲醛反应。
First, epoxy resin reacts with melamine and urea under certain conditions, and then the product reacts with formaldehyde.
以磺化三聚氰胺和尿素为单体，在酸催化下，合成磺化三聚氰胺尿素甲醛树脂。
With sulfonated melamine and urea as monomers and acids as catalysts, the synthesis of sulfonated melamine urea formaldehyde resin is carried out.
以三聚氰胺-甲醛树脂为原料的木材透明防火涂料，具有良好的装饰性能和防火性能。
Transparent fireproof coating for wood based on melamine-formaldehyde resin as raw materials has good decorating property and fireproof property as well.
采用原位聚合法用三聚氰胺-甲醛树脂包覆正十八烷，制备出相变微胶囊。
Phase change microcapsule was prepared by melamine-formaldehyde resin and n-octadecane through in-situ polymerization.
对脲-三聚氰胺-甲醛树脂改性白乳胶进行了研究。
The modified PVAc emulsion adhesive with Urea melamine formaldehyde(UMF) resin is studied.
用热机械分析（TMA）方法研究了三聚氰胺-尿素-甲醛树脂固化初期胶层粘度的变化。
Viscosity change of melamine urea formaldehyde glue line was investigated with a thermo mechanical analyzer (TMA) used as a parallel plates rheometer.
合成了丙烯酰胺改性三聚氰胺(蜜胺)甲醛树脂，研究了其絮凝性能。
Modified melamine formaldehyde resin with acrylamide was synthesized and its flocculability have been studied.
本文介绍尿素-三聚氰胺-甲醛共缩聚合成机理、树脂性能、以及制备工艺对其性能的影响。
The mechanisms of co-condensation, the properties and performance of MUF resin are described in this paper.
本文采用原位聚合法以十二醇为芯材，以三聚氰胺-甲醛树脂为壁材，制备微胶囊相变材料并对其进行性能表征。
The microencapsulated phase change materials were prepared with in situ polymerization using dodecanol as the core, melamine-formaldehyde resin as the shell.
三聚氰胺、尿素与甲醛经羟甲基化、醚化反应，生成甲醚化六羟甲基三聚氰胺和甲醚化羟甲基脲复合树脂胶。
Melamine, urea and formaldehyde underwent hydroxymethylation and etherification to yield a composed resin glue of methyl-etherified hexahydroxy methylmelamine and methyl-etherified hydroxymethylurea.
通过红外光谱(FT - IR)和SEM研究发现，三聚氰胺-甲醛树脂已包覆在APP表面。
The MAPP was analyzed by FT-IR and SEM, the result indicates that melamine resin was coated on the surface of APP.
通过红外光谱(FT - IR)和SEM研究发现，三聚氰胺-甲醛树脂已包覆在APP表面。
The MAPP was analyzed by FT-IR and SEM, the result indicates that melamine resin was coated on the surface of APP.