The corrosion wear resistance of low chromium white cast iron increases when the silicon content increases in it.
而增加含硅量后的低铬白口铸铁的腐蚀磨损耐磨性将比普通白口铸铁的高。
The effect of Si content on the corrosion wear resistance of low chromium white cast iron in the slurry with Cu2+ ion was studied by three-body corrosion wear test.