浇注温度对铸坯的凝固末端位置也有一定影响。
Casting temperature have a little effect on the solidification end location.
较大；钢液浇注温度仅对液芯长度有较大影响。
But the steel temperature only effects on liquid core length.
研究了碲涂料的组成与浇注温度对激冷层的影响。
The effect of te coating and pouring temperature on chilled layer of cast iron are researched.
防止措施是确保足够的随流孕育量，提高浇注温度。
Therefore, in order to prevent the chill defect, it is must to ensure sufficient stream inoculation and to increase the pouring temperature.
为避免产生热裂应适当降低浇注温度，提高型壳温度。
Proper decrease in pouring temperature and increase in shell mold temperature are helpful to preventing hot tear.
浇注温度越高、直浇道空心面积率越大，铝液充型速度越快。
The higher the pouring temperature or the larger the sprue hollow area rate is, the faster the filling velocity of molten aluminum is.
文中叙述了化学成分、离心时间、浇注温度对辊套质量的影响。
The influence of chemical component. centrifugal time and pouring temperature on roll ring quality has been discussed.
合理设计浇注系统、严格控制浇注温度及模壳的温度至关重要。
It's very important to design the gating system reasonably, to accurately controll the pouring temperature and the ceramic shell temperature.
指出了滤饼机制与流动阻力的关系以及对最低浇注温度的要求。
It points out the relationship between the filtration mechanism and flowing resistance, as well as the lowest cast temperature required for molten metal through the cellular ceramic filter.
对高铬铸铁的熔炼速度、过热温度、浇注温度及变质处理进行了研究。
The melting speed, overheat temperature, pouring temperature and modification in production of high chrome cast iron were studied.
结果表明，在不同浇注温度下浇注时，得到的合金显微组织有较大差别。
It is shown that there are apparent differences of microstructure obtained at different pouring temperatures.
对高铬铸铁的熔炼速度、过热温度、浇注温度和变质处理进行了研究。
The influence of melting rate, super heating temperature, pouring temperature and modification on high chromium cast iron were researched.
浇注温度和砂型初始温度越高，热节处粘塑性应变越大，而热应力越小。
The higher the pouring temperature and initial mold temperature are, the larger the plastic strain while the smaller the thermal stress is.
研究表明：模具预热温度影响最大，压射速度次之，浇注温度影响最小。
The results show that mold temperature is the most significant influence factor, injection speed takes the second place, and pouring temperature is the least significant influence factor.
分析了浇注温度、落砂温度对温度场分布、冷却速度、应力和应变的影响。
The influence of pouring temperature and shakeout temperature on the temperature field distribution, cooling velocity, stress and strain was analyzed.
研究了浇注温度、搅拌功率和搅拌时间对A356铝合金的半固态浆料的影响。
It is found that the prepared A356 al alloy semi-solid rheological slurry by the complex method can meet the requirements of rheological casting.
结果表明：碳含量、浇注温度及表面活性元素对试样的变形及组织均有较大影响。
The results showed that the carbon content, pouring temperature and surface active elements have more effect on deformation and structure of the samples.
实验测定了化学成分、浇注温度、铸件模数和铸型刚度对球墨铸铁收缩特性的影响。
The effects of casting modulus, pouring temperature. carbon equivalent and mould toughness on the solidification shrinkage of ductile cast iron was investigated experimentally.
结果表明：在浇注温度和斜坡角度一定时，斜坡长度对坯料显微组织有显著的影响。
It was found that the slope length had great influence on microstructure of the ingots at a certain casting temperature and slope Angle.
研究表明，浇注温度和模壳温度对K423 A合金的组织和性能均具有较大的影响。
The results show that the pouring temperature and shell mould temperature have obvious effect on the microstructure and properties of K423A superalloy.
证明水玻璃白云石砂的溃散性与铸件的大小、壁厚、浇注温度、吃砂量和打箱时间有关。
The collapsibility of the sodium silicate dolomite sand is controlled by the size, wall, pouring temperature, capacity for sand and draw time of the cast.
在检测浇注温度、铸型温度和铸型转速的基础上，用微机实现了对离心铸管机的过程控制。
Based upon the detection of the pouring temperature, and the mould temperature and speed, the process control for centrifugal pipe casting machines is realized by using a microcomputer.
包紧力的大小与铝液浇注温度、成形压力、孔径尺寸、 模型材料的物理性质等有关。
Quantity of enclosed strength is due to cast temperature, shaping pressure , hole dimension, physical property of die material, etc.
提高金属液浇注温度及改良涂料，选用低密度泡沫塑料作模样材料对避免产生分层缺陷有帮助。
To avoid forming layer defect, rising pouring temperature are using improved coating and selecting low density styrofoam pattern are a great help.
采取提高钢质纯净度、控制浇注温度和拉速等改进措施，检测合格率由82.5%提高到92%。
By cleaning molten steel, controlling casting temperature and withdrawal speed, the compliance ration in ultrasonic inspection of plate was enhanced from 82.5% to 92%.
固定浇注温度和铸型温度，研究压射速度和压射比压对压铸am 60 B合金组织与性能的影响。
At proper pouring temperature and mold temperature, the effect of die casting speed and pressure on microstructure and properties of AM60B alloy has been studied.
研究了负压度、模样密度、浇注温度、金属静压头等工艺因素对消失模铸铁件充型速度的影响规律。
The filling speed of lost foam cast iron casting was measured by use of an integrated set of experimental equipment and a specially designed computer acquisition system.
经过分析得出，影响合金流动性和体收缩的主要因素是合金的成分、浇注温度及合金液中含有的夹杂物。
After analysis, the major affecting factor of alloy fluidity and body contraction are compositions, pouring temperature and the inclusions of alloy.
适当提高外加压力和浇注温度有助于渗流过程的进行，但过高的浇注温度和压力对渗流过程都是不利的。
The penetrating casting can be promoted by properly increasing the pressure applied and pouring temperature, but disturbed if pouring temperature and the pressure applied were too high.
适当提高外加压力和浇注温度有助于渗流过程的进行，但过高的浇注温度和压力对渗流过程都是不利的。
The penetrating casting can be promoted by properly increasing the pressure applied and pouring temperature, but disturbed if pouring temperature and the pressure applied were too high.