结果表明该类聚酰胺固化剂具有较普通聚酰胺固化剂粘度低、粘接强度大、韧性大及耐热性好等优点。
It was found that this kinds of polyamides had advantage such as low viscosity, stronger adhesive strength, high flexibility and good heat-resistance over the ordinary polyamides.
指出浅色环氧防静电涂料选用芳脂胺类型的固化剂，所得漆膜的电阻率、防腐蚀性和耐化学品性均优于传统的聚酰胺固化剂。
The result shows: the resistivity, anti-corrosion and chemical resistance of the film from arylated alkyl amine curing agent were better than that of conventional polyamide curing agent.
本文着重从银粉的粒度、添加量和固化剂的种类、用量以及固化条件等方面研究和探讨了环氧-低分子聚酰胺-银粉导电胶体系的导电性及强度。
In this paper the effect of size of silver particles, proportion, curing agent and curing condition on epoxy resin - low - molecular polyamide - silver particles system are studied and discussed.
实验证明，酚醛胺固化剂与低分子聚酰胺的协同效应在一定范围内对固化物强度有较大提高，但酚醛胺的加量并非越多越好。
Test results showed that when the two curing agents were added into the adhesive system within a proper ratio, the strength of the adhesive woule increase.
本文叙述的水性环氧树脂涂料是以环氧树脂为主体、水为分散剂、改性聚酰胺为固化剂的双组分涂料。
The so described water-base epoxy resin coating is a two-components coating with epoxy resin as the main component, modified polyamide as curing agent and water as dispersion medium.
结果表明：与四乙烯五胺相比，低分子聚酰胺作为固化剂时具有较高的反应活性和更为优越的综合性能；
The results show that LMPA curing agent has a higher reactivity and films cured by LMPA have better film properties compared to TPA.
在低分子聚酰胺树脂固化环氧树脂的体系中 ，通过添加一定量的酚醛胺固化剂 ，直接影响该体系的表观及固化物力学性能。
The aperance and the mechanic properties of epoxy resin and low molecular polyamide adhesive system would be affected by the addition of mannich amide.
固化剂聚酰胺加入量也会影响涂层的耐磨性，并对优化设计的耐磨涂层与45钢进行了耐磨对比，其耐磨性是45钢的5倍多。
The ratio of polyamide also affects wear resistance. The coating is more wearable Coatingsteel. Coating s wearability is more than 5 ti…
固化剂聚酰胺加入量也会影响涂层的耐磨性，并对优化设计的耐磨涂层与45钢进行了耐磨对比，其耐磨性是45钢的5倍多。
The ratio of polyamide also affects wear resistance. The coating is more wearable Coatingsteel. Coating s wearability is more than 5 ti…