本发明涉及一种新型醌胺固化剂的制备方法。
The invention relates to a preparation method of a novel quinone amine curing agent.
由优质环氧树脂、改性胺固化剂及活性稀释剂制成；
Use solvent free epoxy resin and high quality epoxy diluents andcuring agents.
指出浅色环氧防静电涂料选用芳脂胺类型的固化剂，所得漆膜的电阻率、防腐蚀性和耐化学品性均优于传统的聚酰胺固化剂。
The result shows: the resistivity, anti-corrosion and chemical resistance of the film from arylated alkyl amine curing agent were better than that of conventional polyamide curing agent.
实验证明，酚醛胺固化剂与低分子聚酰胺的协同效应在一定范围内对固化物强度有较大提高，但酚醛胺的加量并非越多越好。
Test results showed that when the two curing agents were added into the adhesive system within a proper ratio, the strength of the adhesive woule increase.
在低分子聚酰胺树脂固化环氧树脂的体系中 ，通过添加一定量的酚醛胺固化剂 ，直接影响该体系的表观及固化物力学性能。
The aperance and the mechanic properties of epoxy resin and low molecular polyamide adhesive system would be affected by the addition of mannich amide.
胺。常被用作环氧树脂固化剂的化合物。
选用一种液体改性芳香胺为环氧树脂的固化剂，得到了一种适合于树脂传递模塑(rtm)的高性能树脂体系。
Through applying a liquid modified aromatic amine as curing agent for epoxy resin, a high performance resin matrix system for resin transfer moulding (RTM) was derived.
低粘度，室温固化胺类固化剂，特别用于浇铸模具的制作。
Low viscosity, a room temperature curing amine hardener. Specially formulated filler is recommended for casting of patterns and moulds.
本文介绍以TDE- 85环氧树脂作为基体，以间苯二胺(MPD)、间苯二甲胺(A -50)作为固化剂，制备高模量树脂基体的方法。
The prepare method of high modulus resin matrix was introduced, of which epoxy resin TDE-85 was used as matrix, a 50 and MPD were used as curing agents.
低粘度弹力浇铸树脂，建议与先加入的硅微粉和胺类固化剂合用，用于低压电缆的连接。
Low viscosity resilient casting resin. Recommended for pre-filled silica formulations with low caking tendency used with amine curing system for low voltage cable joints.
研究了DCPD酚环氧树脂与酸酐及胺类固化剂的固化反应活性。
It was studied on the curing activity of DCPD phenol epoxy resin with anhydrides and amines.
水性环氧固化剂一般采用多元胺-环氧加成物。
Polyamine - epoxy adduct is used as waterborne epoxy hardener generally.
采用磷酸双氰胺盐作环氧粉末涂料的固化剂、氟化钠作添加剂。
This research USES dicyandiamide as firming agent in epoxy powder coating and sodium fluoride as additive in epoxy.
以环氧树脂为基体，间苯二胺和氨基二苯甲烷的低融点混合物为固化剂，铜粉为导电填料，制备了热固化各向同性导电胶。
Copper conductive adhesives were prepared using epoxy as matrix, the mixture ofm-phenylenediamine and diaminodiphenylmethane as hardener, and copper particles as the con-ducting filler.
低粘度浇铸树脂，建议与胺类和聚肽胺类固化剂组合用于低压电器。
Low viscosity reactive casting resin. Recommended with amine and polyaminoamide curing agents for low voltage electrical and electronic applications.
以环氧树脂为基体，间苯二胺和二氨基二苯甲烷的低融点混合物为固化剂，铜粉为导电填料，制备了热固化各向同性导电胶。
Copper conductive adhesives were prepared using epoxy as matrix, the mixture ofm-phenylenediamine and diaminodiphenylmethane as hardener, and copper particles as the conducting filler.
本文介绍了间苯二胺的各种理化性能、制备方法，以及在环氧固化剂、染料方面的应用情况。
The preparation methods ofm-phenylene diamine, its chemical and physical properties and the USES as curing agent of epoxy resin and dye intermediate were described and reviewed in this paper.
解决了低分子胺类环氧固化剂无法在水中、低温环境中交联固化的问题。
Problems like difficulty for epoxy firming agent of low-molecular amine to be inter-connected and firmed in water or at lower temperatures have been solved.
一种双极板，由包含至少一种环氧树脂、石墨填充物以及作为环氧树脂固化剂的金属胺络合物的组合物制成。
The bipolar plate is made from a composition containing at least epoxy resin, graphite filler and a metal amine complex compound taken as an epoxy resin curing agent.
以环氧树脂、胺加成固化剂、颜料、填料、助剂和混合溶剂为原料研制了彩色环氧地坪涂料。讨论了各组分对涂料性能的影响。
The color epoxy floor coatings are studied. Epoxy resin, polyamide adduct curing agent, pigments, filler, additives and solvent mixture are used as major material.
结果表明：与四乙烯五胺相比，低分子聚酰胺作为固化剂时具有较高的反应活性和更为优越的综合性能；
The results show that LMPA curing agent has a higher reactivity and films cured by LMPA have better film properties compared to TPA.
采用磷酸双氰胺盐作环氧粉末涂料的固化剂、氟化钠作添加剂。
Synthesis of epoxy powder coatings low-temperature curing agent and its application;
介绍了国内外环氧防腐涂料固化剂的发展趋势，指出芳脂胺类型的改性固化剂将全面提升环氧防腐涂料的性能。
The development trent of curing agent for epoxy anti -corrosive paint home and abroad is introduced. The performance of epoxy anti -corrosive paint is improved by using aromatic amine as curing agent.
选用原料己二胺、环氧树脂、丙烯腈合成1种改性固化剂。
Raw materials, hexanediamine, epoxy resin, acrylonitrile were selected and curing agent was synthesized.
优选地，该氨基甲酸酯预聚物是脂族异氰酸酯聚醚预聚物，且该固化剂包括芳族二胺和三醇。
Preferably, the urethane prepolymer is an aliphatic isocyanate polyether prepolymer and the curative includes an aromatic diamine and a triol.
阻燃型胺类环氧树脂固化剂主要包括含磷、舍氮杂环、含硅胺类固化剂，以及舍氮磷杂环和含硅一磷胺类固化剂。
The flame retarded curing agents' mainly included phosphorus-containing, nitrogen - containing, silicon-containing, phosphorus-nitrogen and silicon-phosphorus amines curing agents.
阻燃型胺类环氧树脂固化剂主要包括含磷、舍氮杂环、含硅胺类固化剂，以及舍氮磷杂环和含硅一磷胺类固化剂。
The flame retarded curing agents' mainly included phosphorus-containing, nitrogen - containing, silicon-containing, phosphorus-nitrogen and silicon-phosphorus amines curing agents.
应用推荐