结果表明：与纯低周载荷作用相比，高低周复合载荷下球墨铸铁的裂纹扩展速率明显加快，极大地降低材料的疲劳寿命。
The results show that the crack growth rate under high-low cycle complex fatigue load is greater than that under low cycle fatigue load, and so the fatigue life is obviously reduced.
结果表明：与纯低周载荷作用相比，高低周复合载荷下球墨铸铁的裂纹扩展速率明显加快，极大地降低材料的疲劳寿命。
The results show that the crack growth rate under high-low cycle complex fatigue load is greater than that under low cycle fatigue load, and so the fatigue life is obviously reduced.