The influence of different water-cement ratio on early-age autogenous shrinkage and total shrinkage of concrete under dry condition is experimented in this paper.
进行了不同水灰比对混凝土早期自收缩及干燥条件下总收缩影响的试验研究。
The experimental results show that SCA could either restrain the early autogenous shrinkage of paste or improve the prolonged shrinkage of concrete.
结果表明：复合矿物外加剂可抑制混凝土自收缩变形，并使混凝土长期收缩变形得到补偿。
Increasing autogenous volume expansive deformation for compensating thermal shrinkage deformation of concrete may improve crack resistance.
提高混凝土的自生体积膨胀变形量补偿混凝土的温度收缩变形，对于混凝土抗裂很有意义。
The early cracking of concrete is usually caused by dry shrinkage, autogenous shrinkage of cement hydration and thermal-strain by hydration heat of cement.
混凝土的早期开裂主要是由于混凝土失水所产生的干燥收缩、水泥水化所产生的混凝土自收缩以及水泥水化热所产生的温度应变所引起。
The autogenous shrinkage of HPC develops greatly and mainly during early age due to a low water binder ratio, but there is no standard test method for early autogenous shrinkage of the concrete.
高性能混凝土因水胶比低、自收缩大且主要发生在早期，而目前对于早期自收缩的测量还没有统一标准可依。
The tensile stress induced by restrained thermal and autogenous shrinkage deformations was the main driving force of cracking in concrete at early age.
温度变形和自生收缩变形等受约束形成的拉应力，是引起混凝土早期开裂的主要驱动力；
The tensile stress induced by restrained thermal and autogenous shrinkage deformations was the main driving force of cracking in concrete at early age.
温度变形和自生收缩变形等受约束形成的拉应力，是引起混凝土早期开裂的主要驱动力；