Pretreatment, bluing and post treatment of this process were introduced.
介绍了前处理、发蓝及后处理工序。
The practice shows that proper measures can be taken to effectively prevent red exo-frost on bluing coating.
实践证明，采用适当措施可以有效防止发蓝膜的红色挂霜。
Tapered bores for keyed hubs shall have a minimum of 70% transfer of bluing (surface contact) to the taper gage.
键槽轮毂的锥孔应至少有70%的着色（表面接触）转移到锥度计上？
The invention belongs to the field of surface heat treatment industry, and relates to a bluing antirust furnace.
本发明属表面热处理行业领域，是一种发蓝的防锈炉子。
Adhesion, wear and corrosion resistance of the coatings obtained were compared with those of conventional bluing at room temperature.
测量了发蓝膜的附着力、耐磨和耐蚀性，并与传统常温发蓝进行了对比。
The paper introduces a new technology of bluing in normal temperature with characteristics of high efficiency, energy-saving and non-pollution.
阐述了具有高效、节电、无污染等特点的常温发蓝新工艺。
BLUING / BLUE UP : Process of using blue dye to coat a surface of a master, gauge, or piece of product to check a flat, circular, or tapered surface.
着色检查：使用蓝色染料涂在模具，量规或者产品表面以检查平面、圆面或者锥面的工序。
The results of physical and chemical analysis show that this new bluing process can improve the comprehensive quality further, especially the anticorrosion performance.
产品的理化检验结果表明，新的发蓝工艺能够进一步提高产品的综合性能，特别是耐蚀性。
A new technology and equipment of annealing and bluing for finished stator and rotor of uncoated cold-rolled electric steel lamination in bell-type hytrogen furnace was introduced.
介绍了无涂层电工钢冲片叠片成型后的电机定子和转子在罩式炉内进行退火和发蓝处理一次完成的新工艺及装置。
A new technology and equipment of annealing and bluing for finished stator and rotor of uncoated cold-rolled electric steel lamination in bell-type hydrogen furnace was introduced.
介绍了无涂层电工钢冲片迭片成型后的电机定子和转子在罩式炉内进行退火和发蓝处理一次完成的新工艺及装置。
The production shows that the best bluing time in normal temperature is from 4 to 8 minutes and bluing film is bright and anti-corrosion capacity is at or higher than the specified state standard.
生产实践表明，常温发蓝的最佳发蓝时间为4 ~8分钟，发蓝膜光亮，耐蚀达到并超过国家规定标准。
The production shows that the best bluing time in normal temperature is from 4 to 8 minutes and bluing film is bright and anti-corrosion capacity is at or higher than the specified state standard.
生产实践表明，常温发蓝的最佳发蓝时间为4 ~8分钟，发蓝膜光亮，耐蚀达到并超过国家规定标准。