The ultrafiltration rate of pure water with the coagulation bath temperature increased.
随着凝固浴温度的升高，所成的膜的透水速率上升。
The maximum spinning speed decreased with the coagulation bath concentration increasing.
最大导丝速度也随凝固浴浓度的增大下降。
Porosity increases along with the increasing of coagulation bath temperature, and doesn't have relation to pre-evaporation.
孔隙率随着凝固浴温度的上升而上升，而与预蒸发时间的长短没有关系；
The results showed that the properties of the regenerated bamboo fiber prepared with lower coagulation bath temperature were improved.
实验结果表明：在较低的凝固浴温度下纺制得到的再生竹纤维素纤维的性能较好。
When the coagulation bath concentration is 10%, the maximum of tenacity and modulus and the minimum of extension at break of Lyocell fiber are obtained.
而在凝固浴浓度为10%时，纤维的相对强度和初始模量为最大，延伸度则为最小。
Several spinning procedure conditions were discussed, such as coagulation bath concentration, temperature, extruding rate and core layer liquid flow rate etc.
并对凝固浴浓度和温度、挤出速率、芯液流量等纺丝工艺条件进行了探讨。
Fiber formation, appearance and properties at least depended on spin dope concentration, coagulation bath composition and concentration, and post-spinning draw.
分析认为纺丝液的浓度、凝固浴组成与浓度、拉伸对丝纤维的物理与机械性能均有影响。
The effects of spinning dope concentration, coagulation bath temperature and addition of persimmon leaves on the mechanical properties of blend fiber were studied.
研究了纺丝原液浓度、凝固浴温度、柿叶添加量对共混纤维的力学性能的影响。
The retention rates of Albumin bovine decreases when coagulation bath temperature increases, and first decreases, then increases when pre-evaporation time prolongs.
对牛血清白蛋白的截留率随着凝固浴温度的上升而下降，随着预蒸发时间的延长先略有下降然后上升。
The concentration and temperature of the coagulation bath and spinning conditions all have a great effect on structures and properties of PVDF/PVC hollow fiber membranes.
凝胶浴的浓度和温度、纺丝工艺等都会影响共混体系的相容性并改变膜的结构和性能。
It was noted that when coagulation bath temperature was increased, crystallization could be suppressed, and more porous structure was obtained on the surface of the membrane.
另外，凝胶浴温度升高可以抑制结晶现象，并使膜表面孔径和孔密度增加。
It pointed out that the temperature of spinning solution, negative stretching, temperature of coagulation bath, concentration, flow and spin-finish had influence on quality of flat fiber.
指出原液温度、负拉伸、凝固浴温度、浓度、流量以及所用的油剂都会对扁平纤维的质量产生影响。
The factors affecting the quality of chitin and chitosan fibers were described, including chitin and chitosan quality, solvent for spinning dope and its concentration and coagulation bath.
概述了影响甲壳素和甲壳胺纤维质量的因素，如甲壳素和甲壳胺的品质、纺丝原液的溶剂选择及浓度的确定、凝固浴的确定；
The dense top layer as well as porous supporting layer can be made by duel-bath coagulation method simultaneously.
双凝固浴成膜方法可同时获得较厚的致密表面层和疏松多孔的支撑层。
The dense top layer as well as porous supporting layer can be made by duel-bath coagulation method simultaneously.
双凝固浴成膜方法可同时获得较厚的致密表面层和疏松多孔的支撑层。