Theshrinkage of green body was 0.3% and the density deviation was 0.32%. After infiltrated with molten silicon, the shrinkage of sintering body had another 0.2%.
成型坯体的干燥收缩率小于0.3%，密度分布的标准偏差为0.32%，反应烧结过程中，坯体的收缩率小于0.2%。
With the increase of solids loading, the particle density increases and the bending strength of green body decreases for the network polymer accounting for only a small amount of the composition.
随着固相体积分数的增加，单位面积的颗粒分布密度增大，网络高分子在成分中只占少量，坯体抗弯强度降低。
For the green body containing a certain size of SiC powders, the carbon particle should be less than a certain size, or else, the density and fracture strength of RBSC decrease wit...
对于一定粒度的碳化硅粉而言，加入到生坯中碳粉粒度应小于一定尺寸，否则，陶瓷的断裂强度和密度将随碳粉粒度的增大而降低。
There are some papers proposed adding plasticizer which has di-hydroxyl group structure to improve this bad phenomenon but adding plasticizer will decrease the strength and density of green body.
虽然由过去之文献已知添加具有二羟基结构的塑化剂可改善此种不良现象，但塑化剂的添加往往伴随著薄带强度的降低且对生胚烧结后的致密度有负面的影响。
There are some papers proposed adding plasticizer which has di-hydroxyl group structure to improve this bad phenomenon but adding plasticizer will decrease the strength and density of green body.
虽然由过去之文献已知添加具有二羟基结构的塑化剂可改善此种不良现象，但塑化剂的添加往往伴随著薄带强度的降低且对生胚烧结后的致密度有负面的影响。