HDPE can cause stress cracking easily with affection of environment, which limits its application in industry.
HDPE易受环境的影响产生应力开裂，这限制了其在工业上的应用。
In some of usage environment, the engineering thermoplastics packaging case can cause stress concentration and cracking because of the bad design and processing technology.
热塑性工程塑料包装箱由于设计和加工工艺不当，在各种使用环境中易导致产品应力集中而开裂。
It has been proved that these cracks are caused by sulfide stress corrosion cracking (SSCC) through failure analysis and service environment survey.
通过失效分析和管道服役环境调查，证明开裂原因是管道服役期间发生硫化物应力腐蚀开裂(SSCC)。
At the environment medium, the tubeplate joint welds of titanium reboiler were constantly effected by the alternation stress, welds cracking was occurred in the end.
在环境介质中，钛制再沸器管板接头焊缝长期受交变应力的作用，导致管板焊缝开裂。
The environmental assisted cracking is known as the cracking in material that can be affected by the environment and the stress.
环境辅助裂纹是已知的材料，可以受环境和应力的影响。
A kind of testing machine used to study stress corrosion cracking of materials in natural environment and special environment was introduced, such as toxic atmosphere and corrosion medium.
介绍了一种可以用于研究材料在自然环境及特定环境(如有毒有害气氛、各种腐蚀介质等)下应力腐蚀性能的便携式拉伸应力腐蚀试验装置。
There are some factors which influence the characteristics of initiation and propagation of stress corrosion cracking and corrosion fatigue cracking in high-strength steel in a watery environment.
影响高强度钢在水介质中的应力腐蚀和腐蚀疲劳裂缝萌生和扩展特性的因素甚多。
High environment humidity increases the susceptibility to hydrogen induced cracking and stress corrosion cracking.
高湿度能增大氢致裂纹和应力腐蚀开裂倾向。
High environment humidity increases the susceptibility to hydrogen induced cracking and stress corrosion cracking.
高湿度能增大氢致裂纹和应力腐蚀开裂倾向。