The fiber surface morphology analysed by AFM also approved the result of XPS analysis.
利用AF M对纤维表面形貌分析的结果与XPS结论一致。
Methods with chloroform as the solvent, the PLGA fiber scaffolds with different surface morphology were produced altering PLGA solution concentration and the flowing rate.
方法本实验以氯仿为溶剂，调节plga溶液浓度和流量分别制备了具有不同表面形貌的纤维支架。
The results showed that the extrusion speed had effects on the irregularity of cross section, surface morphology, profile degree, sonic orientation and compactness of PAN fiber.
结果表明：喷丝速度对PAN纤维截面的规整性、表面形貌、异形度、声速取向和致密性等均会产生影响。
A analysis was focused on the chemical composition, morphology and surface characterization of both wheat straw fiber and wood fiber.
本研究从化学组分、纤维形态和表面性质三方面分析比较了麦秆纤维与木材纤维。
The mechanical properties, surface morphology, chemical composition and surface cohesion property of UHMPE fiber were studied before and after surface modification.
研究了处理前后uhmpe纤维的力学性能、表面形貌、化学成分、表面粘结性能的变化。
Many factors such as the surface modification of PVC matrix and cellulose-fiber, processing conditions all affected the cell morphology and physical properties.
多种因素如PVC、纤维素纤维的改性处理、加工条件等都将影响泡孔形态与制品的物理机械性能。
The micro morphology of fiber surface was analyzed by SEM, and the active functional group on the fiber's surface was analyzed by XPS.
利用扫描电镜和电子能谱，进行了纤维表面形貌分析及表面活性官能团分析。
It shows good matrix-carbon fiber adhesion between the treated CF with fracture surface morphology and PA6. the mechanical property of composite is enhanced compared with pure PA6.
复合材料断面照片显示处理后的碳纤维和基体尼龙6材料有着很好的界面结合。
It shows good matrix-carbon fiber adhesion between the treated CF with fracture surface morphology and PA6. the mechanical property of composite is enhanced compared with pure PA6.
复合材料断面照片显示处理后的碳纤维和基体尼龙6材料有着很好的界面结合。