The factors which affect the firing temperature of the glaze were discussed, and the opacifying mechanism of glaze was also approached.
探讨了影响釉烧成温度的诸因素及釉的乳浊机理。
To better visualize this correlation, we plotted the characteristic temperatures given in Table 5 on the graphic of sample height versus firing temperature.
为了更好地想象这种比照，本人们采集了由表格五中样本高像素熄灭温度地图像供给特征温度。
Firing temperature for the production of special circuits in the internal connection and End Lead, PTC thermistors, and semiconductor ceramic device electrodes.
适用于中温烧成制作特种电路的内部连线及端头引出线，PTC热敏电阻及半导体陶瓷器件电极等。
The color glaze of low firing temperature and low expansion coefficient, to match the glaze tile made from common clay, was prepared in lead borosilicate system.
采用铅硼硅熔决釉研制出同时符合普通粘土瓦坯的烧成温度低、热膨胀系数低这两个主要性能特点的釉料。
The color glaze of low firing temperature and low expansion coefficient, to match the glaze tile made from common clay, was prepared in lead borosilicate system.
采用铅硼硅系统，研制出具有低烧成温度、低热膨胀系数的色釉，用作粘土釉面瓦釉料，其外观、物理、化学性能均能满足质量要求。
The high temperature foamed ceramic produced has low firing temperature, short duration of firing, wide range of firing temperature and easily control production.
研制的高温发泡陶瓷具有烧成温度低、烧成时间短、烧成温度范围宽、易于生产控制的特点。
Porcelain: the quality of porcelain has direct relationship with the service life of sits implement. If the firing temperature is higher, the quality of porcelain will be better.
瓷质：瓷质的好坏和马桶的寿命有直接的关系，烧成温度越高，瓷质越好。
It is analyzed that Mossbauer parameter variations of clays from the famous sites of ancient kilns change with firing temperature, firing time and firing atmosphere in firing process.
分析了几种著名的古窑遗址粘土烧制过程中穆斯堡尔参数随烧制温度，烧制时间和烧制气氛的变化规律。
When spodumene was added in the products, the cause for reducing firing temperature, enhancing mechanical strength and heat-shock resistance, possessing good chemical stability was clarified.
阐明在制品中添加锂辉石，能降低烧成温度，提高机械强度，抗热振性以及具有良好的化学稳定性的原因。
Facing main topics are enhancement of dielectric constant of ceramics, decrease of it "s firing temperature. decrease of dielectric layer thickness and keeping reliable contact of electrodes."
提高瓷的介电常数，减小介质层的厚度，保持电极可靠的接触及降低瓷料的焙烧温度是当前的主要研究课题。
The dependences of seepage velocity and bending strength on agglomerant content, forming pressure, particle diameter of the aggregate, soaking time, firing temperature and so on were discussed.
分别从外加粘结剂百分数、成型压力、骨料粒径、保温时间、烧成温度等因素对渗水砖的渗水速度和强度的影响进行了探讨。
The best peak firing temperature was existed, which was between the softening temperature and the peak crystallization temperature, and near the incipient crystallization temperature of the glass.
电阻浆料存在最佳峰值烧成温度。理论分析表明，最佳峰值烧成温度应在软化点与峰值析晶温度之间，靠近起始析晶温度。
Kyanite calcined at two temperatures is used as raw material to prepare calcined kyanite. Their firing temperature, high temperature properties, thermal shock and microstructure have been studied.
用两个温度下煅烧后的蓝晶石为原料，研制烧结蓝晶石制品，对其烧成温度、高温性能、抗热稳定和显微结构作了研究。
As substitution of diopside for talc, the body has lower firing temperature and widening sintering range. The property of diopside porcelain is in keeping with standard of high frequence dielectric.
用透辉石代替滑石时，透辉石瓷有较低的烧成温度和较宽的烧结范围，其性能符合高频电介质标准的要求。
An important part of the souvenir-making is the temperature, which needs to be closely monitored and controlled during the firing process.
制作纪念品最重要是温度，烧火过程中需要仔细检测和控制温度。
The formula of baby and glaze, technological parameter, firing condition, and property of lower-temperature firing porcelain were introduced.
介绍了降低烧成温度的日用瓷的坯釉配方、工艺参数、烧成及瓷质性能。
In firing of machine guns, temperature field of barrel affects the dynamic characteristic directly.
机枪在射击过程中，枪管温度的升高直接影响机枪的动力特性。
The laws of the flame position and the temperature in the HPM changing with the equivalence ratio or the firing rate have been gained.
得出了火焰面位置及燃烧温度随当量比和燃烧强度的变化而在多孔介质中移动的规律；
Temperature difference from top to bottom in preheating zone of tunnel kiln is the biggest obstacle for rapid firing, energy saving.
隧道窑预热带内上下温差过大是实现快速烧成、节能降耗的最大障碍。
The temperature deviation of gas and steam influences the safe operating of large pulverized combustion boiler with tangential firing.
大型四角切圆燃烧锅炉的烟、汽温度偏差对其安全运行具有重要影响。
Aimed at the deviation of gas temperature in the input of level gas flue of six angles tangential firing boiler, the cold modeling test is put on building the test stand by using the modeling theory.
针对六角切圆燃烧锅炉水平烟道入口烟气温度偏差问题，利用模化理论建立试验台，进行冷态模化试验。
By using the double firing process and dihydrate gypsum as the main raw material, white - glazed gypsum ceramic tiles for walls and floors are produced under relatively low temperature.
本文采用二次烧成工艺，以二水石膏为主要原料，在较低温度下制备白色釉面石膏陶瓷墙地砖。
High temperature corrosion, a problem generally met with in boilers firing coal with high sulfur content, may cause leakages in heat delivery surfaces.
高温硫腐蚀是高硫分燃煤锅炉普遍存在的问题，它会引起锅炉受热面泄漏。
In circular firing system, residual rotation of airflow at furnace outlet is the main reason for gas temperature deviation between two sides of furnace outlet and horizontal gas duct.
四角切圆燃烧锅炉炉膛出口气流的残余旋转，是形成炉膛出口和水平烟道两侧烟温偏差的重要原因，可造成高温受热面热偏差和超温爆管。
The characteristics of the firing bed, that is, ventilating evenness, temperature level, gas composition, burn - off rate, are studied, respectively, by means of combustion experiments.
通过燃烧试验，研究了炉前成型煤的层燃特性：通风均匀性、炉温水平、烟气成分、燃烬程度。
Meantime, the suitable ceramic recipe for the kiln is worked out to provide technological conditions for high temperature fasting firing.
同时，研究成功了与窑炉相适应的陶瓷配方，为实现高温快烧提供了工艺技术条件。
Shuttle kiln is an intermittent kiln. When it's being used for firing ceramic products, there is usually a big difference between the indicated temperature and the real temperature of the kiln.
梭式窑炉是间歇性窑炉，在烧制陶瓷产品的过程中，通常会出现测温仪表显示的温度与实际窑炉的温度有较大的误差。
Shuttle kiln is an intermittent kiln. When it's being used for firing ceramic products, there is usually a big difference between the indicated temperature and the real temperature of the kiln.
梭式窑炉是间歇性窑炉，在烧制陶瓷产品的过程中，通常会出现测温仪表显示的温度与实际窑炉的温度有较大的误差。