Abstract: in nuclear power plants, the FAC (flow accelerated corrosion) of carbon steel occurs mainly in the secondary circuit, causing a significant impact on production safety.
摘要：在核电厂中，二回路碳钢管道的流动加速腐蚀(FAC)对安全生产造成很大影响。
Results of weight loss in lab and field site show that corrosion rate of A3 steel can be accelerated flow of seawater, especially in the initial stage.
室内和实海挂片失重测试比较结果表明，海水流动能够加快A3钢在海水中的腐蚀速度，腐蚀初期尤其明显。
Results of weight loss in lab and field site show that corrosion rate of A3 steel can be accelerated flow of seawater, especially in the initial stage.
室内和实海挂片失重测试比较结果表明，海水流动能够加快A3钢在海水中的腐蚀速度，腐蚀初期尤其明显。