The local cleavage fracture stress is mainly determined by the length of the critical microcrack.
细观解理断裂应力主要由临界裂纹的长度决定。
A new method of testing the critical stress intensity factor for stress corrosion cracking based on linear-elastic fracture mechanics theory and stress corrosion cracking theory was put forward.
应力腐蚀临界应力强度因子的测试方法是基于线弹性继裂力学理论和应力腐蚀理论提出的一种新的测试方法。
Blade fracture location is match to the position of maximum stress derived from the static analysis, so try to reduce stress concentration increases the intensity of the blade is critical.
本文研究的叶片的断裂位置与静力分析所求出的最大应力位置吻合，因此设法减小该位置的应力集中情况对于提高叶片的强度很关键。
Fracture toughness (Kc). Critical value of the stress intensity factor for which crack extension occurs.
断裂韧度(Kc)：发生裂纹扩展时应力强度因子的临界值。
Plane strain fracture toughness (KIc). The critical value of the stress intensity factor (i. e., at which crack propagation occurs) for the condition of plane strain.
平面应变断裂韧性(KIc)：平面应变条件下应力强度因子的临界值(即达到该值时裂纹发生扩展)。
Plane strain fracture toughness (KIc). The critical value of the stress intensity factor (i. e., at which crack propagation occurs) for the condition of plane strain.
平面应变断裂韧性(KIc)：平面应变条件下应力强度因子的临界值(即达到该值时裂纹发生扩展)。