High finish rolling temperature promotes the recrystallization of hot-rolled strip, increases favorable texture components, decreases the core loss, and increases magnetic induction of final product.
提高终轧温度可以促进热轧板的再结晶，增加成品中有利织构组分，降低铁损，提高磁感。
But if the annealing temperature is too high these will appear coarse-grained structure resulting from entire recrystallization.
但是，如果温度过高，会因产生再结晶而出现粗晶组织，还会导致性能的严重恶化。
The dynamic recrystallization and recrystallized grain sizes of heading for high-temperature alloy (GH4169) bolt are simulated with this software.
应用该软件分析了高温合金(GH4169)螺栓镦挤工艺的动态再结晶过程和再结晶的晶粒度分布。
Small deformation in high temperature is easy to cause incomplete recrystallization and bulky and uneven grain. It is hard to eliminate them in subsequent rolling process.
高温小变形时容易发生不完全再结晶，造成晶粒粗大且不均匀，在随后的轧制过程中很难消除。
Small deformation in high temperature is easy to cause incomplete recrystallization and bulky and uneven grain. It is hard to eliminate them in subsequent rolling process.
高温小变形时容易发生不完全再结晶，造成晶粒粗大且不均匀，在随后的轧制过程中很难消除。