• The research in flux is mainly to change the original double hot dip coating technique, and change the first hot-dip galvanizing into electrolyzing flux.

    对于研究主要改变原有工艺第一次热镀锌电解助镀。

    youdao

  • Results showed that the coating problem of hot-dip zinc plating workpiece was improved evidently by using the degassing agents MPP230 and MPP620 containing a primary component of polyethylene wax.

    结果发现主要成分聚乙烯脱气MPP230MPP620可以明显改善镀锌件涂装存在的问题

    youdao

  • This paper deals with the role of Ni in coating forming and the effect of Ni on process and property when adding Ni to hot dip Zn bath.

    分析常规热镀锌中加,镍在镀层形成过程中的作用以及镀层工艺、性能影响

    youdao

  • The paper mainly focus on the development of hot dip aluminized coating, and analyzes the composing mechanism of plating process and its microstructure.

    历史进行了简要回顾,分析镀层组织结构形成机理

    youdao

  • The research status about of the microstructure, formation mechanism and growth kinetics of hot dip aluminizing coating is reviewed. Research directions for hot-dip aluminized steel are suggested.

    综述了镀铝层组织形成机理生长动力学和扩散后组织的研究现状,指出了热浸铝钢今后的研究方向

    youdao

  • The surface and cross-section of the pock flaws which appeared on the hot-dip galvanized coating were observed and analyzed by using SEM and energy spectroscopy.

    通过扫描电子显微镜热镀锌钢板镀层表面麻点缺陷表面断面形貌进行了观察对其进行了能谱分析。

    youdao

  • A portable corrosion rate meter was used to comparatively measure the annual corrosion rates of 20 steel tube and its integral hot-dip aluminizing coating in acidic and alkali corrosive mediums.

    采用便携式瞬时腐蚀速度测量仪,20及其铝件分别酸性碱性介质中测定腐蚀速率并进行比较

    youdao

  • The method adopts one or more of casting, hot dip plating, welding, rolling, hot pressing, electroplating and hot spray coating.

    发明可以采用铸造焊接轧制热压电镀、热喷涂一种多种方法生产。

    youdao

  • The white corrosion products on hot dip Zn al alloy coating exposed to seawater in dynamic aerated immersion were investigated by means of XRD and TEM.

    采用XRDTEM铝合金镀层动态充气海水试验时所形成的白色腐蚀产物进行了研究

    youdao

  • Hot dip galvanized coating is the most common and effective way to prevent corrosion of steel.

    热镀锌镀层钢材方法中应用普遍最有效的工艺措施。

    youdao

  • Hot dip galvanized coating is the most common and effective way to prevent corrosion of steel.

    热镀锌镀层钢材方法中应用普遍最有效的工艺措施。