In injection molding, the residual stress and shrinkage of the product are affected by processing conditions directly.
注塑成型工艺参数对制品的最终残余应力和收缩有着直接的影响。
The results show that the shrinkage of injection molding part is increased with thickness of parts in non-linearity, and the increase momentum is moderated with the increase of thickness.
结果表明，制品厚度对其成型收缩的影响很大，制品厚度增大时，注射成型收缩率增大，但这种增大的趋势是非线性的，而是随着厚度的增加而逐渐减缓。
The results show that the interfacial stress produced from the shrinkage of the matrix in the composites injection molding process can strain induced crystallization of th.
结果表明，该共混体系中界面应力的应变诱导致结晶作用及其所引起的基体中伸展链晶体网络结构的形成是该材料实现脆韧转变的重要原因。
The results show that the interfacial stress produced from the shrinkage of the matrix in the composites injection molding process can strain induced crystallization of th.
结果表明，该共混体系中界面应力的应变诱导致结晶作用及其所引起的基体中伸展链晶体网络结构的形成是该材料实现脆韧转变的重要原因。