Finally, examples are given for predicting the fatigue crack initiation life from the tensile properties of steels.
最后给出了根据钢的拉伸性能估算疲劳裂纹起始寿命的实例。
Moreover, the study indicated that the fatigue crack initiation period is the main portion of the total fatigue life at long lives.
该研究还表明，在长寿命范围，裂纹起始寿命是疲劳全寿命的主要部分。
Crack initiation life is much longer than those of low shot peening pressure.
低喷丸强度试件表面微裂纹大量萌生，密度非常高。
The fatigue crack initiation life for standard titanium alloy TC6 specimens is predicted, and the result is consistent with that of the experiment.
利用该方法预估了TC 6钛合金标准件疲劳裂纹萌生寿命，其结果与试验数据吻合。
Especially the contribution to crack initiation life of the ground-air-ground circle in the crack growth formula is underestimated under the transport spectra.
特别是运输机谱中的地—空—地循环，在裂纹扩展的公式中对裂纹形成寿命的贡献估计不足。
The stress whitening can be clearly seen on the fatigue fracture surface and its region is the initiation and nucleation of fatigue crack which is the main part of total fatigue life.
疲劳断口有应力发白现象；应力发白区为疲劳裂纹形核和萌生区，其寿命占疲劳总寿命的大部分；
A calculating method of the total fatigue life of structural joints is proposed based on a study on both the fatigue crack initiation life and crack growth life of joints.
通过对结构疲劳裂纹形成寿命和裂纹扩展寿命的研究，提出了连接件疲劳全寿命的计算方法。
The pre-straining prolonged the fatigue crack initiation life, and increased resistance coefficient and equivalent stress threshold of the fatigue crack initiation.
预应变可以延长疲劳裂纹形成寿命，提高疲劳裂纹形成的抗力系数和裂纹形成的当量应力门槛值；
The crack initiation life and the crack fracture life are the main life of the specimen.
试样寿命主要由裂纹萌生寿命和断裂寿命组成，扩展寿命所占比例较少。
The methods of fatigue crack initiation life predictions under complex load are introduced in this paper.
介绍了复杂载荷下疲劳裂纹形成寿命预测的方法。
A method for crack initiation life prediction of components is presented.
本文提出一种零部件的裂纹形成寿命的类比估算方法。
The fatigue crack initiation life of 300M steel is experimentally investigated and a simple method for predicting the fatigue crack initiation life of materia is offered.
测定了300M钢的缺口疲劳始裂寿命曲线，给出了估算疲劳始裂寿命的方法。
Fatigue crack initiation is an important period in the whole fatigue life. The damage regularity of crack initial period cannot estimate with fracture mechanics which is used in large crack.
疲劳裂纹萌生阶段在整个疲劳破坏过程中占有极为重要的地位，而萌生阶段的裂纹体损伤规律用长裂纹断裂力学方法是无法确定的。
Fatigue crack initiation is an important period in the whole fatigue life. The damage regularity of crack initial period cannot estimate with fracture mechanics which is used in large crack.
疲劳裂纹萌生阶段在整个疲劳破坏过程中占有极为重要的地位，而萌生阶段的裂纹体损伤规律用长裂纹断裂力学方法是无法确定的。
应用推荐