The corrosion wear resistance of low chromium white cast iron increases when the silicon content increases in it.
而增加含硅量后的低铬白口铸铁的腐蚀磨损耐磨性将比普通白口铸铁的高。
The effect of Si and Cu on the corrosive wears resistance of low chromium white cast iron for making grinding body of large grinding ball mill used in mine was studied in the conditions of laboratory.
以大型矿用球磨机研磨体为应用对象，在实验室条件下研究了硅、铜对低铬白口铸铁腐蚀磨损耐磨性的影响。
The low chromium white cast iron had been treated with different cooling rates after 40% deformation .
对低铬白口铸铁经过40 %热变形后，用不同冷却方式下得到的组织与力学性能进行了研究。
The results show that the corrosion wear resistance of low chromium white cast iron decreases with the increase of Cu2 + ion concentration in slurry.
结果表明，当浆料介质中铜离子浓度增加时，低铬白口铸铁的腐蚀磨损耐磨性降低。
The effect of Si content on the corrosion wear resistance of low chromium white cast iron in the slurry with Cu2+ ion was studied by three-body corrosion wear test.
而增加含硅量后的低铬白口铸铁的腐蚀磨损耐磨性将比普通白口铸铁的高。
The effect of Si content on the corrosion wear resistance of low chromium white cast iron in the slurry with Cu2+ ion was studied by three-body corrosion wear test.
而增加含硅量后的低铬白口铸铁的腐蚀磨损耐磨性将比普通白口铸铁的高。