Experiments on deoxidation with al for ZL18A steels were carried out. The effect of s content on nonmetallic inclusion was observed.
对ZL 18 A钢进行了用铝脱氧、控制钢中夹杂物和酸溶铝含量的研究。
The results showed that the major cause of longitudinal surface cracking of 20 steel tube blanks was higher nonmetallic inclusion content in the steel than standard value.
结果表明：非金属夹杂物超标是导致管坯表面产生纵向裂纹的主要原因。
The results showed that the major cause of longitudinal surface cracking of 20 steel tube blanks was higher nonmetallic inclusion content in the steel than standard value.
结果表明：非金属夹杂物超标是导致管坯表面产生纵向裂纹的主要原因。