The technical investigation of relieving residual stress on the surface of rectangular cold drawn section by means of high temperature heat treatment was provided.
提出用高温近火方法来改善矩形截面冷拔型钢表面残余应力的工艺探索。
The effect of some lapping parameters, such as: abrasives size, lapping pressure and lapping speed, on the residual stress at surface of work-pieces was discussed.
探讨了固着磨料研磨中磨料尺寸、研磨压力和研磨速度等研磨参数对工件已加工表面残余应力的影响规律。
In this paper, the influence of diamond tool sharpness on machined surface quality was studied from the viewpoints of the cutting force, surface roughness and residual stress.
本文从切削力、表面粗糙度、表面残余应力几个方面，研究了金刚石刀具刃口修锐度对切削表面质量的影响。
The experiments have been shown that the three factors of residual stress microstructure as well as surface roughness including in the all factors of SI have most influence on the FFR.
试验结果表明，表面完整性中的残余应力、组织结构与表面粗糙度这三个因素对疲劳断裂抗力是最有影响力的三个因素。
It is analyzed of the residual stress generating procedure in adhesive coating layer on the surface of port crane parts for the purpose of surface protection or repairing.
分析了用于港机部件表面保护和修复的涂层中通常存在的内应力的产生过程，认为它是导致涂层早期破坏的主要原因之一。
The production mechanism of the surface residual stress producing in grinding process is the combined effect on extrusion stress and the cutting stress and the thermal load.
在磨削加工过程中产生表面残余应力，其产生机理是磨粒刃作用引起的挤压应力和切削应力及热应力的综合作用效应。
The effects of cutting speed and feed on residual stress of workpiece machined should be studied to improve surface quality in machining.
在切削加工中，为了提高已加工工件的表面质量，需要研究切削速度和进给量对已加工工件残余应力的影响规律。
The research on the relation of surface residual stress and alloy performance has theoretical significance.
研究硬质合金表面残余应力与合金性能之间的关系有一定的理论意义。
Investigation was made of effect of preplastic deformation for unexplosive and explosive treatments on strength, surface residual stress and hydrogen embrittlement of the specimens.
研究了预塑变对爆轰处理和未爆轰处理样品的强度、表面残留应力、氢脆敏感性及其关系的影响。
The results show that the welding residual stress on the outer surface and on the inner surface behave quite differently with heated band width.
结果表明，管子内、外侧残余应力和加热宽度表现出不同的规律：管子外侧的残余应力随加热宽度的增加缓慢下降；
The results indicate that the elastic operating stress range of a torsional axis is extended greatly by pre-twist process and the main reason lies on surface residual stress.
结果表明，预扭后扭力轴弹性工作应力范围得到极大扩展，其主要原因在于预扭塑变形成的表面残馀应力。
The influences of carburizing heat treatment process and grinding process on surface residual stress of automobile gears are studied.
研究了渗碳热处理过程中淬火冷却和回火状况以及磨削加工对渗碳淬火汽车齿轮表面残余应力的影响。
The formation factors of residual stress for on line grinding roller surface during cold rolling strip were studied.
对冷轧带钢在线磨辊辊表层残余应力的形成因素进行了研究。
The effect of broaching rate and feed per tooth, tool orthogonal rake on residual stress of workpiece surface are analyzed by Broaching GH761 Alloy.
这里分析了GH761 合金拉削时，速度、齿升量、拉刀前角对拉削表面残余应力的影响。
The analysis on fatigue cracks of the outer race of aero-bearing shows that the distribution of residual tensile stress on race surface could reduce its contact fatigue life.
航空轴承外圈的疲劳裂纹分析表明，套圈表面的残余压应力分布致使轴承表面接触疲劳寿命降低。
Quantitative analyses have been made on the composition of corroded products and the macro-residual stress on the pipe surface by EDX and XRD.
应用x射线能谱仪和x射线衍射仪分别对腐蚀产物及管表面宏观残余应力进行定量分析。
The results show that the effect of alternate load on surface residual stress relaxation of aluminum alloy plate mainly depends on the vector superposition of load stress and residual stress;
结果表明：交变载荷对铝合金板表面残余应力松弛的影响主要取决于加载应力与残余应力的矢量叠加；
The results show that the effect of alternate load on surface residual stress relaxation of aluminum alloy plate mainly depends on the vector superposition of load stress and residual stress;
结果表明：交变载荷对铝合金板表面残余应力松弛的影响主要取决于加载应力与残余应力的矢量叠加；