In this paper, one-part room temperature vulcanized silicone rubber (RTV-1) adhesive is prepared for assembling composite insulator.
研究了一种用于合成绝缘子组装的单组分室温硫化硅橡胶(rtv - 1)。
107 room temperature vulcanized silicone rubber and calcium carbonate, white carbon black, additives such as mixing, vacuum glass glue.
可将107室温硫化硅橡胶和碳酸钙、白炭黑、助剂等混合均匀，抽真空制成玻璃胶。
High thermal conductive room temperature vulcanized silicone rubber could be prepared by filling with different particle size distribution or surface treated fillers.
指出通过填充不同粒径分布的填料或对填料进行适当的表面处理，可以制备高导热室温硫化硅橡胶。
With hydroxyl group terminated PDMS on both side as feedstock, adding several kinds of fillers and adjuvants, the room-temperature vulcanized silicone rubber coatings are prepared.
以二羟基聚二甲基硅氧烷（PDMS）为基体，加入不同填料和助剂，制备了室温硫化硅橡胶涂层。
Room Temperature Vulcanized (RTV) silicone rubber coating can prevent pollution flashover accident from happening, and it has been widely used in China.
室温硫化硅橡胶涂料(rtv涂料)可以有效防止污闪事故，已在我国电力系统中广泛应用。
Room temperature vulcanized (RTV) silicone rubber can effectively prevent the secondary discharge on space high-voltage array.
室温硫化硅橡胶(rtv胶)可以有效防止空间高压太阳阵产生二次放电事件。
The influence factors on surface curing time of silicone rubber release agent vulcanized at room temperature were analyzed by experiments.
通过实验分析了影响室温硫化硅橡胶脱模剂表面固化时间的各种因素。
With hydroxyl group terminated PDMS on both side as feedstock, adding several kinds of fillers and adjuvants, the room-temperature vulcanized silicone rubber coatings are prepared.
采用一定粘度的聚二甲基硅氧烷为基体，加入适量填料和助剂，成功制备了室温硫化硅橡胶涂层。
The room temperature vulcanized (RTV) silicone rubber coating on the surface of insulator can incrcase the flashover voltage of insulators due to the migration of hydrophobicity of RTV coating.
研究了环境温度、硅橡胶的分子量、交联程度和涂层厚度等因素对憎水迁移特性的影响并对憎水性迁移机理问题进行了讨论。
The room temperature vulcanized (RTV) silicone rubber coating on the surface of insulator can incrcase the flashover voltage of insulators due to the migration of hydrophobicity of RTV coating.
研究了环境温度、硅橡胶的分子量、交联程度和涂层厚度等因素对憎水迁移特性的影响并对憎水性迁移机理问题进行了讨论。