The salt spray corrosion resistance performances of several single inhibitor and composite inhibitor have been studied by the salt spray corrosion test.
通过盐雾试验，考察了几种防锈剂及其复合防锈剂的抗盐雾性能。
This article has described the structure, operation principle and test method of salt spray cabinet, and discussed various factors that influence the cycle corrosion test.
介绍了盐雾试验箱的构造，工作原理和试验方法，并探讨了涂层在循环腐蚀试验中的诸多影响因素。
Chemical property testing: salt spray test of materials, corrosion test of stainless steel.
化学性能测试：材料的盐雾试验、不锈钢腐蚀试验等。
The correlativity between neutral salt spray accelerated test and atmospheric corrosion test in Shijiazhuang was studied by the mass loss determination of 45 steel, A3 steel, 20 steel and gun steel.
以45钢、A3钢、炮钢、20钢为金属试样，研究它们在中性盐雾加速试验及石家庄大气环境暴露试验中腐蚀失重与时间的变化规律。
The corrosion resistance of deposits and covering power of the plating bath were tested respectively by neutral salt spray test and inner-pole method, and the hardness of deposits was also measured.
采用中性盐雾试验测定了镀层的耐蚀性，采用内孔法测定了镀液的覆盖能力，并测定了镀层的硬度。
The corrosion resistance of 07X16H6 precipitation hardening stainless steel in tempered state was studied using high temperature oxidation, salt-spray test and stress corrosion test.
通过高温抗氧化、盐雾腐蚀和应力腐蚀试验研究了07X16H6沉淀硬化不锈钢在使用状态（回火态）时的耐蚀性能。
The concentration of salt and the relative areas of the large cathode coupled with a small magnesium alloy anode have an important effect on the accelerated galvanic corrosion in salt spray test.
盐雾实验中，盐的浓度、大阴极小阳极的面积比以及阴极材料相对于镁阳极的尺寸是加速镁合金电偶腐蚀的重要因素。
Salt spray test machine for a variety of surface materials by electroplating, anodizing, painting, rust-proof oil, anti-corrosion treatment, testing its products on the corrosion resistance.
盐水喷雾试验机针对各种材质之表面经电镀、阳极处理、喷涂、防锈油等防腐蚀处理后、测试其制品之耐腐蚀性。
The salt spray test results of piston rods with different surface qualities showed that superfinish process of piston rods before plating can improve corrosion-resistance of piston rods significantly.
不同表面质量的连杆盐雾试验对比表明：镀前对汽车减振器连杆进行表面超精加工可显著提高连杆的耐蚀性。
The corrosion resistance of renovated film was measured by batch salt spray test.
采用间隙盐雾试验考察了修复层的耐蚀性能。
Corrosion resistance of aluminum tube surface with silane-rare earth composite coating was studied by electrochemical means, weight loss and salt spray test respectively.
采用电化学、失重和盐雾实验对铝管表面硅烷稀土复合膜的耐蚀性进行考察。
Corrosion resistance of aluminum tube surface with silane-rare earth composite coating was studied by electrochemical means, weight loss and salt spray test respectively.
采用电化学、失重和盐雾实验对铝管表面硅烷稀土复合膜的耐蚀性进行考察。