The microstructure and properties of chromium bronze after homogenizing treatment, solid solution and aging treatment, cool deformation and aging was studied.
研究了均匀化处理、固溶时效、冷变形时效等对铬青铜显微组织和性能的影响。
The effect of cooling regime after solid solution and aging treatment on hardness, electrical conductivity and impact toughness was investigated for Cu-Ni-Be alloy.
本文研究了固溶时效后不同冷却方法对铜镍铍合金的硬度、电导率和冲击韧性的影响。
The results showed that multiple solution and aging treatment had a significant effect on increasing plastic property and fracture toughness, although had little effect on strength.
结果表明：多重固溶时效热处理可以显著提高合金的塑性和断裂韧度，而对强度的影响不大。
The external oxidation will lead to chromium dilution in the surface layer of alloy, and the internal oxidation will decrease the strengthening effect of solution and aging treatment.
外氧化使合金表面贫铬；内氧化将降低合金固溶时效强化效果。
However, large grain size and continuous grain boundaries combine to produce stress concentrations, thus lowering the plasticity and impact value of alloy after solution and aging treatment.
而粗大的晶粒及连续的晶界容易产生应力集中，因此合金经固溶时效后具有较低的塑性和冲击值。
It is shown that the mechanical properties of annealed sample of 2224 aluminum alloy are improved by the combination of solid solution and aging treatment after ECAP, the size of grain is refined.
结果表明，退火态2224铝合金经e CAP挤压后，进行固溶和时效处理，明显提高了合金的力学性能，细化了合金的晶粒。
Hard anodizing film could be obtained on Al-Cu alloy surface which had been treated with solid solution treatment and natural aging.
经固溶处理和自然时效的铝铜合金可以进行硬质阳极氧化。
This paper is about construction and characteristics of C194, which are effected by heat-treatment of solution and aging .
研究了C194合金变形与固溶时效热处理工艺条件对其组织性能的影响。
The results show that the required high hardness can't be achieved after forging and solution-aging treatment.
结果发现，通过锻造和固溶时效均不能有效地达到所要求的高硬度。
The results show that the required high hardness can't be achieved after forging and solution-aging treatment.
结果发现，通过锻造和固溶时效均不能有效地达到所要求的高硬度。