It has been proved that these cracks are caused by sulfide stress corrosion cracking (SSCC) through failure analysis and service environment survey.
通过失效分析和管道服役环境调查，证明开裂原因是管道服役期间发生硫化物应力腐蚀开裂(SSCC)。
Based on the NACE standard, the behavior of restriction on hydrogen induced cracking (HIC) and sulfide stress corrosion cracking (SSCC) of X80 grade pipeline steel was investigated.
依据NACE标准研究了X80级管线钢的抗硫化物应力腐蚀开裂(SSCC)和氢致开裂(HIC)行为。
The mechanism and general influence factors of sulfide stress corrosion cracking (SSCC) of chemical equipment made of high strength steel are summarized.
系统的综述了高强钢化工设备硫化物应力腐蚀开裂机理及常规的影响因素。
The sulfide stress cracking is one of the reasons of gas transmission pipeline failure.
硫化物应力腐蚀是引起输气管道失效的主要原因之一。
The resistance of nitrided J55 casing to sulfide stress cracking (SSC) was studied by C-ring testing and three-point bending testing under different conditions.
用应力环腐蚀试验和三(四)点弯曲试验研究了某J 55(即石油套管)渗氮套管在不同试验条件下的腐蚀行为，并和未渗氮套管的抗腐蚀性进行了比较。
The resistance of nitrided J55 casing to sulfide stress cracking (SSC) was studied by C-ring testing and three-point bending testing under different conditions.
用应力环腐蚀试验和三(四)点弯曲试验研究了某J 55(即石油套管)渗氮套管在不同试验条件下的腐蚀行为，并和未渗氮套管的抗腐蚀性进行了比较。