UV-curable adhesive is a class of important material that could be rapidly created adhesive bonding properties by the UV radiation.
紫外光固化胶粘剂是指借助UV辐射使粘接材料快速产生粘接性能的一类胶粘剂。
UV-curable adhesive monomer 10-methacryloyloxydecyl thiophosphoric acid dichloride was synthesized from the reaction of thiophosphoryl chloride with methylacrylic acid and 1,10-decanediol.
以甲基丙烯酸、1，10-癸二醇和三氯硫磷为主要原料合成出了紫外光固化粘接性单体10-甲基丙烯酰氧癸基硫磷酸二氯。
In this paper, research progress of the photo-initiators and their applications in UV curable adhesive were reviewed.
综述了光引发剂以及它们在紫外光固化粘合剂中的应用研究进展。
The optimal formula of the UV curable conductive adhesive gained from single factor test was as follows: Silver-plated copper powder 70%, complex photoinitiator 4%, AIBN 2% and KH570 2.5%.
通过单因素实验确定了导电胶的最佳配方：镀银铜粉填充量为70%、复合光引发剂用量为4%、热引发剂aibn用量为2%、偶联剂KH570用量为2.5%。
The optimal formula of the UV curable conductive adhesive gained from single factor test was as follows: Silver-plated copper powder 70%, complex photoinitiator 4%, AIBN 2% and KH570 2.5%.
通过单因素实验确定了导电胶的最佳配方：镀银铜粉填充量为70%、复合光引发剂用量为4%、热引发剂aibn用量为2%、偶联剂KH570用量为2.5%。