It was found that the solidification cracking susceptibility of weld metal increases remarkably as nickel content increases.
结果表明:随着焊缝中含镍量的增加,焊缝金属的凝固裂纹敏感性增大。
The improvement of microstructure leads to a considerable reduction of the susceptibility of hot cracking of weld metal as indicated by the transverse-varestraint test.
增加焊缝中的共晶数量并改善其分布形态,从而有助于降低焊缝金属的热裂纹敏感性。
Disadvantages include risk of hydrogen cracking in carbon steels and weld metal porosity in aluminium alloys.
缺点是在碳钢中有氢致裂纹、铝合金中有焊缝气孔产生的危险。
In this paper, the temperature field of weld metal solidification cracking in the stainless steel was analyzed and simulated.
进行了不锈钢焊接凝固裂纹温度场分析与数值模拟。
Neodymium can increase weld metal hot cracking susceptibility of the pure nickel electrode used for cold welding of cast iron.
纯镍铸铁焊条中加入稀土钕会增加焊缝热裂敏感性。
Neodymium can increase weld metal hot cracking susceptibility of the pure nickel electrode used for cold welding of cast iron.
纯镍铸铁焊条中加入稀土钕会增加焊缝热裂敏感性。