In frequent bending stress condition, fatigue cracking occurred due to the cracking source had been initiated in welding heat affected zone.
在承受频繁的弯曲应力作用后,在其焊接热影响区萌生了裂纹源进而发生疲劳开裂。
The transformation superplasticity in welding CGHAZ (Coarse Grain Heat Affected Zone) of EH36MOD steel and its effect on fatigue life have been studied with thermal simulating method.
采用热模拟方法,对EH36MOD钢焊接热影响区粗晶区(CGHAZ)的相变超塑性及其对疲劳寿命的影响进行了研究。
The joint which is connected by welding method is called the welding joint, which is composed of welding seam, fusion zone, heat affected zone and its adjacent base metal.
用焊接方法连接的接头称为焊接接头,它由焊缝、熔合区、热影响区及其邻近的母材组成。
The effects of high temperature pre-precipitation on the stress corrosion properties of the heat affected zone were also studied after welding.
并研究了高温析出对焊接热影响区及后处理应力腐蚀性能的影响。
Owing to heat action during X80 pipeline steel welding the organization and performance of heat affected zone will change considerably in particular of coarse grain heat affected zone (CGHAZ).
X80管线钢在焊接过程中,热影响区由于受到焊接过程热的作用,其组织和性能会发生较大的变化,尤其是粗晶热影响区的组织和性能变化最大。
Using the heat of welding to vapour water, cooling rates are lowered on the weld bead and heat -affected zone.
利用焊接时的加热使水汽化,不仅使焊道而且使热影响区的冷却速度减慢。
Modeling of the heat affected zone in welding is a difficult problem in dynamic analysis, while the consistent of modal parameters is a major objective of modeling and model amendment.
焊接热影响区建模是动力学分析的一个难点问题,而模态参数的一致逼近是建模及修正的一个主要目标。
Due to the advantage of high energy density, low heat affected zone, low shape distortion of components, high welding speed, the research of the laser welding is the focus of the laser process.
激光焊接技术由于其能量密度高、热影响区小、焊接变形小、焊接速度高等众多优点,一直是激光加工方面的研究热点。
Moreover, the fatigue crack growth rates of the weld metal and heat affected zone are lower than those of the base metal. Having excluded the effect of welding residual tress...
在排除焊接残余应力导致的裂纹闭合效应后,焊缝及热影响区疲劳裂纹扩展速率与基材相当。
This paper analyzes the welding performances of the pipeline steel X80 including softening of heat affected zone, its matching with base material and the possibility of welding cracking. It also de…
文章分析了高强度X80钢管道的热影响区的软化、焊缝金属与母材的匹配及产生焊接裂纹的可能性,介绍了管道环缝焊接工艺,还列举了国外X80钢管道的焊接工程实例。
In welding test of TCS stainless steel, it was found that impact absorbing energy of heat-affected zone (HAZ) near bond line in welded joint was low.
在TCS不锈钢前期焊接试验中发现其焊接接头热影响区的冲击吸收功值在熔合线附近较低,原因是接头热影响区晶粒粗大所致。
Microstructure and mechanical properties changing rules of 2219 Al-alloy HAZ (heat-affected zone) with twin wire welding were studied using welding thermal simulation method.
采用焊接热模拟试验方法研究了2219铝合金双丝焊热影响区的微观结构和力学性能的变化规律。
The variation of microstructure and mechanical properties of the welding heat-affected zone of 2090 Al-Li alloy were investigated by means of the welding thermal, simulated and strain cycles test.
采用焊接热模拟试验方法研究了在焊接热循环和应力-应变循环同时作用下,2090铝锂合金焊接热影响区显微组织和力学性能的变化特征。
The welding method used was a PC-GMAW process with mixture gases shielding. Central crack for the welded plate was located in the fusion zone between welding seam and heat-affected zone.
焊接方法为脉冲熔化极混合气体保护焊,焊接板的中心裂纹处于焊缝与热影响区之间的熔合区。
Central crack for the welded plate was located in the fusion zone between welding seam and heat-affected zone.
焊接板的中心裂纹处于焊缝与热影响区之间的熔合区。
The effect of welding line energy on microstructure and low temperature toughness of heat-affected zone(HAZ) of X70 pipeline steel was studied by welding thermal simulation method.
采用焊接热模拟技术、显微组织分析和冲击试验的方法,研究了焊接线能量对X70管线钢焊接热影响区组织和低温韧性的影响规律。
In welding test of TCS stainless steel, it was found that impact absorbing energy of heat-affected zone (HAZ) near bond line in welded joint was low. The reason is coarse grain in HAZ.
在TCS不锈钢前期焊接试验中发现其焊接接头热影响区的冲击吸收功值在熔合线附近较低,原因是接头热影响区晶粒粗大所致。
The hardness of welded joints obtained by double-wire submerged arc welding is significantly better than that obtained by CO2 gas shielded. The peak hardness appears in the heat affected zone.
CO2气体保护焊接头的硬度值明显较双丝埋弧焊接头的硬度值高,硬度值在热影响区出现峰值。
The basic requirement of welding the steel 2205 is that the weld metal and heat-affected zone obtain a favorable phase balance and retain the performance as the base metal after welding.
平衡铁素体和奥氏体两相组织在焊缝金属和热影响区中的比例,保证焊接接头的性能,是双相不锈钢焊接的基本要求。
The coarse primary ferrite appeared in weld metal, and coarse bainite appeared in heat-affected zone under larger heat input welding condition, which caused low...
在较大焊接热输入条件下焊接,焊缝金属产生粗大先共析铁素体、过热区产生粗大粒状贝氏体,焊接接头低温冲击韧性因此降低。
The coarse primary ferrite appeared in weld metal, and coarse bainite appeared in heat-affected zone under larger heat input welding condition, which caused low...
在较大焊接热输入条件下焊接,焊缝金属产生粗大先共析铁素体、过热区产生粗大粒状贝氏体,焊接接头低温冲击韧性因此降低。
应用推荐