The most reason of cracking breakout is badness of arc and high temperature of molten steel and high withdrawal speed.
对弧不良、钢水温度高、拉速快是造成裂纹漏钢的主要原因；
By cleaning molten steel, controlling casting temperature and withdrawal speed, the compliance ration in ultrasonic inspection of plate was enhanced from 82.5% to 92%.
采取提高钢质纯净度、控制浇注温度和拉速等改进措施，检测合格率由82.5%提高到92%。
By cleaning molten steel, controlling casting temperature and withdrawal speed, the compliance ration in ultrasonic inspection of plate was enhanced from 82.5% to 92%.
采取提高钢质纯净度、控制浇注温度和拉速等改进措施，检测合格率由82.5%提高到92%。