本文研究了单向纤维增强复合材料的热膨胀性能。
The thermal expansion properties of unidirectional fiber reinforced composites were studied in this paper.
测定了复合材料中不同复合比对热膨胀性能的影响。
The effect of component ratio (in % of volume) on thermal expansion was measured.
并对制备的复合材料进行显微组织观察和热膨胀性能分析。
The microstructure and thermal expansion property of the composite were observed and analyzed.
氟硅酸盐微晶玻璃的热膨胀性能主要取决于微晶玻璃的晶相组成及其相对含量。
The thermal expansion coefficient of fluosilicate glass-ceramics is mainly affected by the crystal phases and their amount.
借助于DSC/TG和XRD测试手段，对水泥石的热膨胀性能变化规律进行了机理分析。
The mechanism of thermal expansion of hydraulic cement paste is also re searched with DSC/TG and XRD methods.
这个发现与基于间隔条材料与浮法玻璃之间热膨胀系数差异而预期的性能一致。
This finding is in keeping with the expected performance based on the difference in thermal expansion coefficients between spacer material and float glass.
本文研究了氧化锂加入量对低温熔块的熔融温度、力学性能、热膨胀系数的影响。
The influences of lithia content on the melting temperature, mechanical properties and thermal expansion coefficient of low temperature frit were studied.
合成材料具有更好的承载能力，更低的热膨胀系数，更好的耐磨性和更好的抗疲劳性能。
The composite material has resulted in greater load carrying capacity, a reduced thermal expansion, greater wear resistance and fatigue endurance.
采用铅硼硅熔决釉研制出同时符合普通粘土瓦坯的烧成温度低、热膨胀系数低这两个主要性能特点的釉料。
The color glaze of low firing temperature and low expansion coefficient, to match the glaze tile made from common clay, was prepared in lead borosilicate system.
研究了增强相和界面对这三种复合材料的热导率和热膨胀系数的影响，并对这些性能进行了理论分析和数值模拟。
The effects of reinforcer and interface on the thermal conductivity and CTE of the composites were investigated, and the properties were analyzed and simulated.
应用热膨胀测试、抗折强度测试和可见光透过率测试分析了微晶玻璃的性能。
The performances are studied by means of heat expansion testing, intension testing and visible light transmission testing and so on.
采用铅硼硅系统，研制出具有低烧成温度、低热膨胀系数的色釉，用作粘土釉面瓦釉料，其外观、物理、化学性能均能满足质量要求。
The color glaze of low firing temperature and low expansion coefficient, to match the glaze tile made from common clay, was prepared in lead borosilicate system.
性能测试包括热膨胀系数、差热曲线和电性能等。
The thermal expansion coefficient DTA and electrical properties were also investigated.
在低温陶瓷结合剂中添加适量金属或合金粉，就会对结合剂的耐火度、流动性、热膨胀系数、强度等性能产生影响。通过试验分析，合金粉的加入能改善结合剂的强度及韧性。
When Added Additive, PEC, strength, the ratio of the thermal expansion and fluidity etc, of bond would be effected, through testing, strength and toughness of bond will proved with adding alloy.
文章阐述了热膨胀阻水油膏的研制过程及制作工艺，给出了该热膨胀阻水油膏的性能测试指标。
In this paper, its development process and manufacturing techniques are described and the performance test data given.
研究了利用金矿尾砂熔制玻璃的方法，测定了基础玻璃的抗折强度、化稳性、密度、热膨胀性等理化性能。
In this article, the method of producing the glass from the goldmine-tails has been studied, and the bending strength, chemical stability, density, thermal expansivity of the glass have been measured.
因此，本阀具有极高的耐磨损、耐腐蚀、耐冲蚀性能，且隔热性好、热膨胀小。
Therefore, this valve has a very high wear resistance, corrosion resistance, erosion resistance, and good insulation, thermal expansion.
一种超高导热、低热膨胀系数的复合材料及其制备方法，属于高性能功能材料领域。
The composite material with very high heat conductivity and low heat expansion coefficient and its preparation process belongs to the field of high performance functional material.
该产品具有优异的耐焊性和耐湿性，低热膨胀系数以减少变形，优异的温度循环性能和较佳的流动性。
This product is of excellent solder resistance and moisture resistance, low-heat expansion coefficient to reduce distortion, excellent temperature recycle performance and good fluidity.
它不但具有非常好的机械加工性能、高导电性和低热膨胀系数，还具有优异的力学性能、抗氧化性能和抗热震性。
In addition to good workability, high conductivity and low thermal expansion coefficient, it has excellent mechanical properties, excellent oxidation resistance and excellent thermal shock resistance.
它不但具有非常好的机械加工性能、高导电性和低热膨胀系数，还具有优异的力学性能、抗氧化性能和抗热震性。
In addition to good workability, high conductivity and low thermal expansion coefficient, it has excellent mechanical properties, excellent oxidation resistance and excellent thermal shock resistance.
应用推荐