By comparing backgouging of plasma arc with carbon arc to the welded joint of 13-5 martensitic stainless steel, the backgouging of plasma arc is proved feasible for the full penetration weld.
通过对13 -5型马氏体不锈钢焊接接头进行等离子弧清根及碳弧气刨清根的比较，证明等离子弧清根对全焊透焊缝实施背面清根是可行的。
It was found that impact toughness of weld metal was maximum using carbon arc air gouging, and it was minimum using acid backing.
结果表明，清根方式对焊缝冲击韧度有明显影响，用碳弧气刨清根得到的焊缝冲击韧度最好，而用酸性衬垫得到的焊缝冲击韧度最差。
The method of Carbon arc-welding is adopted. It is feasible in practice to be used in the material weld. The feedback from the user demonstrates the reliability of welding quality.
焊接方法采用碳弧焊，通过生产实践验证是可行的，用户在使用中对产品的反馈论证了其焊接质量的可靠性。
The method of Carbon arc-welding is adopted. It is feasible in practice to be used in the material weld. The feedback from the user demonstrates the reliability of welding quality.
焊接方法采用碳弧焊，通过生产实践验证是可行的，用户在使用中对产品的反馈论证了其焊接质量的可靠性。