The thermal decomposition kinetics of cardanol-formaldehyde polymers has been studied by non-isothermal thermogravimetry.
用非等温热重法研究了代森锰锌的热分解反应动力学。
Cardanol modified phenolic formaldehyde resin was synthesized by using phenol 100 PHR, cardanol 40 PHR and adding an additive agent.
用100份苯酚(以质量计)，加入40份腰果酚，并加入一种助剂合成腰果酚改性酚醛树脂。
Cardanol -aldehyde ferric polymers were prepared by condensation polymerization with formaldehyde, n-butyl aldehyde, furfural and iron trichloride.
以溶液缩聚法，由腰果酚分别与甲醛、正丁醛、糠醛和三氯化铁制备了腰果酚醛铁聚合物。
The paper analyses the structure, curing conditions and the properties of the cardanol resol which can be made from cashew nut oil produced in Hainan Island.
采用我国海南岛产腰果油制得的槚如果酚合成了高邻位热固性酚醛树脂，并对所合成的树脂的结均、固化条件、固化后树脂的性能进行了分析。
The invention provides application of cardanol in epoxy resin curing. In the process of using, the weight ratio of the cardanol to the epoxy resin is 1-60:100.
本发明提供了腰果酚在环氧树脂固化中的用途，在使用的过程中，腰果酚和环氧树脂之间的重量比为1 - 60∶100。
Condensation polymers from cardanol, formaldehyde and amine (PCX) are systhesized by copolycondensation, then are reacted with epoxy resin to form coating films.
用共缩聚的方法，由腰果酚、甲醛和多元胺合成腰果酚缩醛胺聚合物。
The films remain properties of both cardanol-formaldehyde resin and epoxy resin , which are acid-resisting , alkali-resisting and organic solvent-tolerant, and also have good service time.
该聚合物与环氧树脂形成的涂膜兼具酚醛树脂型和环氧树脂型涂膜的优异性能，耐酸、碱和有机溶剂，而且使用期较长。
The films remain properties of both cardanol-formaldehyde resin and epoxy resin , which are acid-resisting , alkali-resisting and organic solvent-tolerant, and also have good service time.
该聚合物与环氧树脂形成的涂膜兼具酚醛树脂型和环氧树脂型涂膜的优异性能，耐酸、碱和有机溶剂，而且使用期较长。