Results showed that the coating problem of hot-dip zinc plating workpiece was improved evidently by using the degassing agents MPP230 and MPP620 containing a primary component of polyethylene wax.
结果发现，主要成分为聚乙烯蜡的脱气剂MPP230与MPP620可以明显改善热浸镀锌件涂装存在的问题。
The surface and cross-section of the pock flaws which appeared on the hot-dip galvanized coating were observed and analyzed by using SEM and energy spectroscopy.
通过扫描电子显微镜对热镀锌钢板镀层表面麻点缺陷的表面和断面形貌进行了观察，并对其进行了能谱分析。
This paper deals with the role of Ni in coating forming and the effect of Ni on process and property when adding Ni to hot dip Zn bath.
分析了在常规热镀锌浴中加镍后，镍在镀层形成过程中的作用，以及对镀层工艺、性能的影响。
The paper mainly focus on the development of hot dip aluminized coating, and analyzes the composing mechanism of plating process and its microstructure.
对热浸铝的历史进行了简要回顾，分析了其镀层组织结构及形成机理。
The research status about of the microstructure, formation mechanism and growth kinetics of hot dip aluminizing coating is reviewed. Research directions for hot-dip aluminized steel are suggested.
综述了热浸镀铝钢镀铝层的组织、形成机理、生长动力学和扩散后组织的研究现状，指出了热浸镀铝钢今后的研究方向。
A portable corrosion rate meter was used to comparatively measure the annual corrosion rates of 20 steel tube and its integral hot-dip aluminizing coating in acidic and alkali corrosive mediums.
采用便携式瞬时腐蚀速度测量仪，对20钢及其热浸镀铝件分别在酸性和碱性介质中测定年腐蚀速率并进行比较。
The method adopts one or more of casting, hot dip plating, welding, rolling, hot pressing, electroplating and hot spray coating.
本发明可以采用铸造、热浸镀、焊接、轧制、热压、电镀、热喷涂等一种或多种方法生产。
The white corrosion products on hot dip Zn al alloy coating exposed to seawater in dynamic aerated immersion were investigated by means of XRD and TEM.
采用XRD和TEM对热浸锌铝合金镀层在动态充气海水全浸试验时所形成的白色腐蚀产物进行了研究。
The research in flux is mainly to change the original double hot dip coating technique, and change the first hot-dip galvanizing into electrolyzing flux.
对于助镀剂的研究主要是改变原有的双热浸镀工艺，改第一次热浸镀锌为电解助镀。
Hot dip galvanized coating is the most common and effective way to prevent corrosion of steel.
热镀锌镀层是钢材防蚀方法中应用最普遍的、最有效的工艺措施。
Hot dip galvanized coating is the most common and effective way to prevent corrosion of steel.
热镀锌镀层是钢材防蚀方法中应用最普遍的、最有效的工艺措施。