The corrosion weight loss rate and impact toughness of high Mn steel in hot concentrated caustic solution were studied by using immersed corrosion, impact test and SEM.
采用浸泡腐蚀试验和腐蚀前后的冲击试验并借助于扫描电镜观察,研究了热强碱介质中高锰钢的腐蚀速率和冲击韧度。
The corrosion weight loss rate and impact toughness of high Mn steel in hot concentrated caustic solution were studied by using immersed corrosion, impact test and SEM.
采用浸泡腐蚀试验和腐蚀前后的冲击试验并借助于扫描电镜观察,研究了热强碱介质中高锰钢的腐蚀速率和冲击韧度。