Rubber, Silicone resin, BDR (Butadiene resins).
橡胶，硅胶树脂，丁二烯树脂。
First, we synthesized the common silicone resin.
本文首先是合成耐高温有机硅树脂。
MQ silicone resin to finalize the optimum conditions.
最终确定MQ硅树脂的最佳分解工艺条件。
Borders and glass components of the gap filled with silicone resin.
边框和玻璃组件的缝隙用硅酮树脂填充。各边框间用角键连接。
Polyurethane coating system modified with silicone resin is introduced?
介绍有机硅改性聚氨酯涂料的工艺及性能。
The thermodegradation of GS-401 ablative silicone resin was studied with TG, DTA and IR.
我们用热重、差热和红外光谱法研究了GS-401烧蚀有机硅树脂的热降解反应。
Synthesis of MQ silicone resin and its application in silicone pressure sensitive adhesive;
本文主要介绍了压敏胶粘剂所用增粘树脂的种类、特征及其选用的方法。
The flame retardant modification of polycarbonate (PC) with methyl-phenyl silicone resin is studied.
采用苯基甲基硅树脂对聚碳酸酯(PC)进行阻燃改性。
By the glass fiber yarn woven into a tube at high temperature treatment, silicone resin coating to form.
是由玻璃纤维纱编织成管后经高温处理，涂以有机硅树脂而成。
The silicone resin is used in the form of a particulate with an average particle size of less than 700 mum.
所述有 机硅树脂以平均粒度小于700微米的颗粒形式使用。
Liquid alkoxysilyl -functional silicone resins, method for their preparation, and curable silicone resin compositions.
液态烷氧基甲硅烷基官能的硅氧烷树脂，其制备方法，及可固化硅氧烷树脂组合物。
Silicone resin modified polyester(SP) is a kind of ultra-pure surface protection material used in semiconductor device.
聚酯改性硅漆（SP）是用于硅器件表面保护的高纯绝缘材料。
Silicone fiberglass sleeving, woven as sleeving by non-alkali fiberglass and coated with silicone Resin in high temperature.
该产品采用无碱玻璃纤维编织成套管，然后经高温处理，并涂有机硅共聚树脂而成。
This paper focuses on the development and application of the composites based on phenolic resin , silicone resin and phosphate.
重点介绍了酚醛树脂、有机硅树脂、磷酸盐等系列耐烧蚀复合材料的研究进展及应用。
The methyl phenyl silicone resin for heat resistant coatings was prepared by converse hydrolysis-polycondensation of chlorosilane.
采用逆水解法进行氯硅烷水解—缩聚反应，制备了适用于耐高温涂料的甲基苯基硅树脂。
The reinforcing effectiveness mainly depends on the structure of MQ silicone resin including M/Q ratio and the content of hydroxyl groups.
MQ硅树脂对缩合型双组分室温硫化硅橡胶的增强效果主要决定于MQ硅树脂的结构，包括M/Q和硅羚基的质量分数；
The silicone resin marine anti-fouling coating was prepared by using NaPT as the marine anti-fouling agents and silicone resin as the basic material.
以苯甲酸钠为防污剂、硅树脂为基料，制得硅树脂海洋防附着涂料。
Both acrylate-based polymer and silicone resin were proposed as recoating materials for broadband wavelength tuning and temperature compensation of LPFG.
分别采用丙烯酸类聚合物与硅树脂材料实现了长周期光纤光栅（LPFG）的大范围波长调谐与温度补偿。
Silicone acrylic resins can be either the reaction product of a silicone intermediate with acrylic monomers, or a cold blend of silicone resin and acrylic polymers.
硅丙烯酸树脂是由硅树脂和丙烯酸单体反应而得到的产品，或是硅树脂和丙烯酸类聚合物的共混物。
The silicone resin is synthesized using hydrolysis-polycondensation method from phenyl and methyl chlorosilane, and the factors influencing this synthesis are investigated.
以甲基和苯基氯硅烷为单体，采用水解缩聚的方法合成有机硅树脂，并对影响有机硅树脂合成的有关因素进行了研究。
The thermal conductive coating was obtained with the epoxy modified silicone resin as matrix, and the mixture of silicone nitride and alumina as the heat conductive fillers.
以环氧改性有机硅树脂为基体，氮化硅、氧化铝混合填料为导热粒子制备了导热绝缘涂料。
The polysiloxane glue in the formulation may be replaced by commercial silicone oil, silicone rubber and silicone resin for improved high temperature performance in the air.
也可用各种商品的硅油、硅橡胶和硅树脂代替本配方的聚硅氧烷胶料从而提高它们在空气中的耐高温性能。
The molecular structure of the silicone resin pre-and post-blending modification by poly (butyl methacrylate)(PBMA) was characterized by Fourier transform infra-red spectrometry.
采用傅里叶变换红外光谱表征了聚甲基丙烯酸丁酯（PBMA）共混改性有机硅树脂前后的结构特征；
Synthesis process of the discussion MQ silicone resin performance of the main factors such as reaction ratio, reaction time, reaction temperature, vinyl add content, add water and so on.
讨论合成过程中影响MQ硅树脂性能的主要因素如反应配比、反应时间、反应温度、乙烯基添加含量、加入水量等。
The varieties and morphologies of silicone resin products, as well as the synthesis and application of methyl silicone resin and methyl phenyl silicone resins are described in this paper.
介绍了有机硅树脂的品种及产品形态，以及甲基硅树脂和甲基苯基硅树脂的合成及应用。
The effect of sintering process and glass content on the coating properties was researched. A heat-resistant silicone resin is selected as a good coating of organic material by TGA and IR test.
将玻璃填料、有机硅树脂、溶剂等其它助剂按一定比例配制成高温涂料，进行耐高温性、柔韧性、干燥时间、附着力等性能的测试。
After finished with silicone resin, the anti felt shrinkage and warp and wept shrinkage of 100% wool worsted fabric could be kept in "machine washable" standards with other feature index excellent.
采用有机硅树脂对精纺纯毛织物进行防毡缩整理，整理后的织物面积毡缩率、经向和纬向收缩率都达到“机可洗”标准，其他各项性能指标都较好。
After finished with silicone resin, the anti felt shrinkage and warp and wept shrinkage of 100% wool worsted fabric could be kept in "machine washable" standards with other feature index excellent.
采用有机硅树脂对精纺纯毛织物进行防毡缩整理，整理后的织物面积毡缩率、经向和纬向收缩率都达到“机可洗”标准，其他各项性能指标都较好。