The best content of DOP was 10 phr for CPE/NBR blends, DCP from 1 to 2 phr, TAIC 2 phr.
适量增塑剂能提高该共混体系的性能，最佳用量为10份。DCP、TAIC的最佳用量分别为1~2份和2份。
The effect of two kinds of additives(PDM, TAIC)on the properties of EPDM/MVQ blends was investigated.
研究了PDM和TAIC两种助硫化剂对共混胶性能的影响。
The equilibrium swelling method showed that the crosslinking degree of TAIC was higher than that of PDM.
用平衡溶胀法测试共混物的交联密度，表明TAIC共混胶的交联程度大于PDM共混胶。
The tensile strength, elongation at break and tear strength of TAIC were higher than those of PDM while the compression set was opposited.
随着硫化助剂用量增加，TAIC共混胶的拉伸强度、拉断伸长率和撕裂强度均大于PDM共混胶，而压缩永久变形的变化率正好相反。
The results indicated that the gel content of cured liquid EPDM had variance hardly with increasing the amount of DCP, however, increased with increasing the amount of TAIC.
结果表明，液体EPDM的凝胶含量随dcp的增加无明显变化，随taic的增加而增加；交联产物的拉伸性能有相似的变化趋势。
The results indicated that the gel content of cured liquid EPDM had variance hardly with increasing the amount of DCP, however, increased with increasing the amount of TAIC.
结果表明，液体EPDM的凝胶含量随dcp的增加无明显变化，随taic的增加而增加；交联产物的拉伸性能有相似的变化趋势。