TG-FTIR analysis shows that the thermal degradation of resin matrix mainly happens in the first step.
热红联用分析表明,基体的降解主要发生在热失重第一阶段。
The effect of lanthanum oxide on thermo-oxidative degradation behavior of LLDPE was studied by thermogravimetry, oxidation induction time measurements, rheological and TG-FTIR analyse.
通过热失重、氧化诱导期、流变分析和热重-红外联用分析等方法研究了氧化镧对LLDPE热氧分解行为的影响。
This paper firstly makes experiments on wood combustion in anoxic surroundings with method of TG-FTIR analysis. The influence of Oxygen concentration on TG of wood combustion is thoroughly analysed .
采用TG—FTIR分析方法深入研究了火场中硬木地板材料和棉花秆缺氧变氧浓度燃烧过程,深入分析了氧浓度对燃烧热失重过程的影响;
The pyrolysis behavior and characteristics of filled polytetrafluoroethylene (PTFE) are studied in the atmosphere of nitrogen with TG-DSC-FTIR and TG.
采用TG - DSC - FTIR、TG技术研究了填充聚四氟乙烯(PTFE)在氮气气氛下的热解行为与热解规律。
TG analysis shows that, with temperature increasing, anhydride formation is occurred first, and confirmed by the FTIR bands.
TG分析结果表明,随温度的升高,首先形成了酸酐,这可由FTIR光谱确定。
The heat resistant poly(lactic acid) was studied, the structure and properties were characterized by FTIR, DSC, TG, X-ray diffraction, heat shrinkage and breakage strength.
研究了一种耐热聚乳酸,并对其进行了红外光谱、示差扫描量热分析、热重分析、X-射线衍射、热收缩及断裂强力等测试。
Ptentiodnamic polarization, FTIR, and TG were applied to investigate the structure and electrochemical performance of inhibitive water-soluble polyaniline.
运用电化学动态极化法、红外光谱和热重等分析方法研究了缓蚀水溶性聚苯胺的结构性能和缓蚀机理。
The crystal structure and outward appearance, IR property and thermal stability of the organic-anion-pillared hydrotalcites have been studied by XRD, TEM, FTIR and TG-DTA.
通过XRD、TEM、FTIR、TG-DTA等多种表征手段分别对有机阴离子柱撑水滑石的晶相结构及其影响因素、晶体形貌、红外性能、热稳定性进行了研究。
The structures, chemical components and properties of the acquired products at room temperature were characterized and analyzed by XRD, Element analysis, SEM, FTIR, TG-DSC and Spectrum analysis.
用常温下的X射线衍射谱、元素分析、扫描电镜、红外光谱、热分析及光谱分析对产物的常温结构、组分及性质进行了表征。
Transitional metal complexes of pyromellitic acid were synthesized by homogeneous precipitation method, and characterized by TG, element analysis and FTIR.
用均匀沉淀法合成了均苯四甲酸过渡金属配合物。
The structure and properties of the hybrid coatings were studied by FTIR spectroscopy, SEM, TG and test experiment of film performance.
采用FTIR、SEM、TG和涂膜性能实验等对复合涂料的结构和性能进行了研究。
The molecular structure of this product has been validated again by FTIR and TG.
产品分子结构分别用红外光谱分析和热重分析进行了验证。
The structure identification and the element content analysis were investigated with scanning electron microscope, plasma spectral analysis, TG analysis, 13c NMR and FTIR spectral analysis.
本文通过扫描电镜、等离子体光谱分析、热重分析、13c核磁共振波谱分析、傅立叶红外变换光谱分析,对它进行物质结构的鉴定和元素含量分析。
The structure identification and the element content analysis were investigated with scanning electron microscope, plasma spectral analysis, TG analysis, 13c NMR and FTIR spectral analysis.
本文通过扫描电镜、等离子体光谱分析、热重分析、13c核磁共振波谱分析、傅立叶红外变换光谱分析,对它进行物质结构的鉴定和元素含量分析。