The Charpy impact test of base metal, weld and heat affected zone of X80 grade pipeline steel of certain factory was conducted, and its effective grain was researched.
对某厂x 80高钢级管线钢母材、焊缝、热影响区进行了夏比冲击韧性试验，对其有效晶粒进行了研究。
The concept of "weld bead heat affected zone"(WBHAZ) was proposed.
提出了“焊道热影响区”的概念。
The properties in weld deposit metal and Heat Affected Zone are strictly homogeneous with the base metal.
在焊接性能和热影响区金属矿床严格均匀与金属基材。
The fracture rod has cracks in the microstructure of weld zone, intergranular cracks exists in the coarse grain zone of the weld heat affected zone.
进一步比较了断裂拉杆和已经产生裂纹的拉杆焊缝区的显微组织，发现在焊缝的热影响区粗晶区存在沿晶裂纹。
The influence of weld heating on microstructure of heat affected zone was investigated in this paper.
探讨了焊接加热对热影响区组织的影响。
The results show that the TIG weld joint of ZM5 magnesium alloy is composed of heat affected zone, partially melted zone and weld metal.
结果表明：ZM5合金TIG焊接接头是由热影响区、部分重熔区和焊缝组成。
The microstructure in weld metal, heat affected zone (HAZ) doesn't change, but the grains in HAZ grow up.
焊缝金属、热影响区中的微观组织基本没有变化，但热影响区组织晶粒略有长大趋势。
It can also avoid pretermission of plating, burnout of zinc layer on weld beam and heat affected zone, and other limitations on the inner surface of fuel tank made of galvanized sheet.
从而避免了传统电镀锌板直接焊接成型油箱内表面漏镀、焊缝及热影响区锌层烧损等缺陷。
The fracture toughness of the weld metal is lower than that of the base metal and the fracture toughness of heat-affected zone (HAZ) is intervenient between those of weld metal and base metal.
接头焊缝金属的断裂韧度显著低于母材，而热影响区断裂韧度则介于母材和焊缝金属之间。
Using the heat of welding to vapour water, cooling rates are lowered on the weld bead and heat -affected zone.
利用焊接时的加热使水汽化，不仅使焊道而且使热影响区的冷却速度减慢。
Micro characteristic of cracks propagation research: the path of crack propagation in the heat-affected zone and weld metal is the mix of transgranular and intergranular.
裂纹扩展的微观特征研究：在热影响区与焊缝区的裂纹扩展均为沿晶与穿晶混合型。
The result shows that the fracture mode is low stress brittle fracture. The fracture is mainly caused by needle type martensite in the heat affected zone of the weld joint.
结果表明，在连接杆焊缝附近的热影响区中存在大量针状马氏体组织，在低应力的作用下，导致材料发生脆性断裂。
Metallurgical tests of cross-sectional weld samples indicate a minimal heat-affected zone that is identical to the parent metal.
剖焊样品的金相检验表明，成品的最小热影响区与母体金属完全相同。
Stress-strain tests show that: the weld residual stress and the fusion zone is relatively concentrated, the residual stress of the heat affected zone is relatively small.
应力应变测试表明：焊缝与熔合区是残余应力比较集中的地方，热影响区的残余应力比较小。
Moreover, the fatigue crack growth rates of the weld metal and heat affected zone are lower than those of the base metal. Having excluded the effect of welding residual tress...
在排除焊接残余应力导致的裂纹闭合效应后，焊缝及热影响区疲劳裂纹扩展速率与基材相当。
Cracking resistance of ultra-low cabon Cu-bearing age-hardening steels was studied in this paper by computing, maximum hardness in weld heat-affected zone test and Y-groove cracking test.
采用理论计算、热影响区最高硬度试验和小铁研试验方法研究了超低碳含铜时效钢的抗裂性。
The fatigue crack growth (FCG) behavior of the weld heat-affected zone of 14MnNbq bridge steel was systematically investigated in this paper.
从最弱链模型的物理本质出发，探讨了影响焊接热影响区脆性断裂的主要因素。
The coarse primary ferrite appeared in weld metal, and coarse bainite appeared in heat-affected zone under larger heat input welding condition, which caused low...
在较大焊接热输入条件下焊接，焊缝金属产生粗大先共析铁素体、过热区产生粗大粒状贝氏体，焊接接头低温冲击韧性因此降低。
The basic requirement of welding the steel 2205 is that the weld metal and heat-affected zone obtain a favorable phase balance and retain the performance as the base metal after welding.
平衡铁素体和奥氏体两相组织在焊缝金属和热影响区中的比例，保证焊接接头的性能，是双相不锈钢焊接的基本要求。
The basic requirement of welding the steel 2205 is that the weld metal and heat-affected zone obtain a favorable phase balance and retain the performance as the base metal after welding.
平衡铁素体和奥氏体两相组织在焊缝金属和热影响区中的比例，保证焊接接头的性能，是双相不锈钢焊接的基本要求。