High chromium-Molybdonum wear-resistant alloys are hypoeutectic white cast iron.
高铬钼抗磨合金本质为亚共晶型高合金白口铸铁。
The results obtained can spread the application of the hot-deformed white cast iron.
所得结果对改善白口铁脆性扩大其应用具有重要的指导意义。
The abrasiveness of white cast iron with low alloy content was studied through abrasion test.
通过磨损试验研究了变形对低合金耐磨铸铁耐磨性的影响。
The effect of hot deformation amount on impact toughness for Vanadium white cast iron was studied.
研究了热变形量对钒白口铸铁冲击韧性的影响。
As cast martensite high chromium white cast iron has good wear resistance and high impact toughness.
马氏体铸态高铬铸铁具有良好的抗磨、耐蚀和强韧性。
The low chromium white cast iron had been treated with different cooling rates after 40% deformation .
对低铬白口铸铁经过40 %热变形后，用不同冷却方式下得到的组织与力学性能进行了研究。
The improvement of white cast iron integrated mechanical property by inoculation and heat treatment is suggested.
本文提出了一种改善白口铸铁综合机械性能的方法——变质处理和热处理。
The corrosion wear resistance of low chromium white cast iron increases when the silicon content increases in it.
而增加含硅量后的低铬白口铸铁的腐蚀磨损耐磨性将比普通白口铸铁的高。
The high chromium white cast iron was carried on wear abrasion test under different loads on the testing machine.
对不同载荷作用下的高铬铸铁在耐磨实验机上进行了磨料磨损试验；
A new procedure for repair welding of white cast iron roller is presented and analysis is carried out to the results.
介绍了白口铸铁轧辊焊接修复新工艺，并对其结果进行了分析。
The application of the medium Mn white cast iron containing Re showed this material has a better commercial efficiency.
对稀土中锰白口铁进行了生产性试制，并经应用，其经济效益显著。
This paper highlights the experiment results in improving the toughness and hardness of white cast iron by heat treatment.
介绍了通过热处理提高白口铸铁硬度和韧性的试验结果。
The thermal fatigue behavior of white cast iron with different quantity of deformation has been investigated in the paper.
本文对不同变形量白口铸铁的热疲劳行为进行了探讨。
The surface of the hypoeutectic white cast iron of great wearable work piece in common use was treated by laser hardening.
对要求高耐磨的大型工件常用的亚共晶白口铸铁材料进行了不同条件的激光表面强化处理。
Effect of residual austenite on mechanical properties and abrasion resistance of medium Mn white cast iron was investigated.
研究了残余奥氏体对中锰白口铸铁力学性能和抗磨性的影响。
The result shows that the abrasion capability of Ct-white cast iron has compact relations with its composition and microstructure.
结果表明铬系白口铸铁的抗磨料磨损性能与其成分和组织有着密切的关系。
The effect of multi element alloying on the microstructure and properties as cast of high chromium white cast iron has been studed.
本文研究了多元合金对高铬白口铸铁铸态组织和性能的影响。
Our country is rich in tungsten resources. Taking tungsten as the main alloy element, tungalloy white cast iron liner is developed.
我国钨资源丰富，以钨为主要合金元素，开发了钨合金白口铸铁衬板。
Under high stress or low stress abrasion working conditions, high Cr white cast iron can be used just after it having been air quenched.
高应力磨料磨损或低应力磨料磨损工况条件下，高铬白口铸铁空淬后不须回火可直接应用。
The results show that the modification of white cast iron by RE can change the carbide morphology and distribution and increase the toughness.
用稀土变质处理中锰白口铁可改变碳化物形貌及分布且提高其韧性。
Adopting forging method and proper heat treatment after forging can improve significantly the impact toughness of chromium alloy white cast iron.
利用锻造方法并结合锻后适当的热处理工艺可大幅度提高铬合金白口铸铁的冲击韧性。
By purifying the alloy melt, refining matrix grain and carbide, it is possible to increase the impact toughness of the Cr-alloyed white cast iron.
通过净化合金液，细化基体晶粒，细化碳化物可使铬合金白口铸铁的冲击韧性提高。
Variation and failure of the grinding ball of high chromium white cast iron during production and service are mainly caused by the internal stress.
内应力是造成高铬白口铸铁磨球在生产和服役过程中出现变异和失效的主要原因。
The microstructure and mechanical properties of a new type wear-resistant white cast iron with the boride as wear-resistant phase were investigated.
研究以硼化物为耐磨相的新型耐磨白口铸铁的组织特点与力学性能。
The carbides types, techniques preparation, microstructure, property, and applications range of three kinds of chromium white cast iron were introduced.
分析了三种铬系白口铸铁的碳化物类型、制备工艺、组织形貌、性能特点以及应用范围。
Increasing the corrosion potential of the matrix not only reduces the inter-phase corrosion speed but also raises the corrosion resistance of white cast iron.
提高基体的腐蚀电位，不仅可以降低相间腐蚀速度，而且可以大幅度提高铬系白口铸铁的耐蚀性。
The ways of improving the toughness of white cast iron Were reviewed by means of low-alloying, modification, hot plast deformation, casting and heat treatment.
从低合金化、变质处理、热塑性变形、铸造和热处理等几个方面，综述了国内提高普通白口铸铁韧性研究的进展情况。
The modern advanced metallurgy casting, management and information are important content of modern scale production of high chrome white cast iron grinding ball.
现代先进的冶金铸造技术、现代管理和信息技术是更好地实现高铬白口铸铁磨球的现代规模化生产的重要内容。
The current status of research work, production technique and application on high chromium white cast iron are introduced and its research trend is also discussed.
介绍了高铬白口铸铁的研究、生产工艺和应用情况；并对高铬白口铸铁的研究方向提出了看法。
The current status of research work, production technique and application on high chromium white cast iron are introduced and its research trend is also discussed.
介绍了高铬白口铸铁的研究、生产工艺和应用情况；并对高铬白口铸铁的研究方向提出了看法。