凝结时间和安定性均符合要求。
The setting time and soundness of samples accord with request.
为了控制其凝结时间，需加入2%的缓凝剂。
In order to control its coagulation time, 2% retarder should be added.
外加剂的掺量可由凝结时间一电动电位曲线确定。
The volume can be confirmed by curve of setting time and electrokinetic potential relation.
试验结果表明，水玻璃能显著加快水泥浆的凝结时间。
The results showed that silicate can significantly speed up the setting time of cement grout.
凝结时间则由复合体中占比例较多的一种水泥所控制。
Its setting time is determined by the cement which is the majority in this compound cement.
阐述了水泥中不可忽视的一项重要技术指标- 凝结时间。
The paper elucidates that for cement an important technical index-setting time, which must not be neglected.
研究了骨胶蛋白质石膏缓凝剂对石膏凝结时间和强度的影响。
The effect of bone glue protein retarder on setting time and strength of gypsum is studied.
研究了不同掺量、不同细度的几种粉煤灰对水泥凝结时间的影响。
The effect of several fly ash with different amount and fineness on the setting time of cement is studied.
碱磷渣胶凝材料的凝结时间较短，但都可以达到硅酸盐水泥标准。
The setting time of alkali-activated phosphor slag cement is short, but they all adjust to the standards of Portland cement.
研究了磷酸盐、含钙材料对水玻璃—矿渣水泥的凝结时间的影响。
This paper studies the influence of phosphate, calcareous material on set time of water glass-slag cement.
建筑石膏中掺入S型缓凝剂可使凝结时间显著延缓，但强度略有降低。
When the s type retarder is added to the plaster, the setting time of plaster is delayed significantly and the strength is a little lower.
上述外加剂对砂浆强度和水泥凝结时间的影响也是本研究的部分内容。
Effect of the above admixtures on strength of mortars and setting of cement paste were measured.
该水泥烧成温度低、凝结时间快、早期和后期强度都高、耐侵蚀性能好。
The cement has advantages of low sintering temperature, fast coagulation time, high initial and later strength and good corrosion resistance.
考察各种缓凝剂对建筑石膏凝结时间、硬化体强度以及结晶习性的影响。
The effect of retarder on setting time, strength of hardened paste and crystallization habit of building gypsum was studied.
最好的凝结时间上的同时雾化雾化低于第一反应物含有液体温度第二液进行。
Preferably, the condensation takes place on a simultaneously atomized second liquid of lower temperature than the atomized liquid containing the first reactant.
考察了SAE对水泥砂浆的密度、吸水性、凝结时间以及水泥水化速度的影响。
The effects of SAE on the density, absorbency, setting time and cement hydration of cement mortars were studied.
在水泥中加入磷石膏做缓凝剂，对凝结时间影响较大，但对强度影响不太明显；
Phosphorous gypsum makes cement condensation time prolonged, while give no evidence influence on cement strength.
介绍了石膏含量对含钡铁铝酸盐水泥的水化、抗压强度和凝结时间等性能的影响。
The effect of gypsum content on the hydration, compressive strength and setting time of Ba-bearing aluminoferriate cement was presented.
针对国外自动维卡仪需要人工进行分析得出凝结时间，提出了数据自动分析和处理。
Relatively to coagulation time tested on overseas automatic Vicat apparatus which is gained through manual analyses, data automatic analysis and disposal have been put forward.
对掺加粘结剂的脱硫石膏的凝结时间、压折强度、保水性能、剪切粘结强度的测试。
Testing the setting time, flexural strength, compressive strength, water retention, adhesive strength of gypsum with the adhesive agents.
添加剂使石膏的凝结时间略有延长，添加剂的加入使石膏模型的吸浆厚度略有减小；
The set time of plaster mould by adding additives is almost the same as usual. The ability of plaster mould to resist alkali corrosion increases by adding additive.
结果表明，矿渣细粉对水泥标准稠度需水量基本没有影响，但延长了水泥的凝结时间。
The results showed that the ultrafine slag did almost not influence the needed water of cement, but it postponed the setting time.
结果表明：钢渣的掺入可以改善水泥浆体的流动性，凝结时间随钢渣掺量增加而延长。
The results show that mobility of cement paste was improved after adding steel slag and setting time extends with the addition of steel slag increasing.
研究了宝钢转炉滚筒渣、电炉渣代砂建筑砂浆的和易性、强度、凝结时间和收缩等性能。
The workability, strength, setting time and shrinkage of cement mortars with Bao Steel rotating furnace slag (BSRS) or electric furnace slag (EFS) as substitute for sand were studied.
研究了影响碱-粉煤灰-碱矿渣水泥(AAFSC)的强度的因素。测定了其凝结时间。
The influence factors of Alkali - activated - Fly ash - Slag cement (AAFSC) on strength were investigated and the setting time of AASFC was determined.
结果表明，三元复合缓蚀剂具有良好的缓蚀效果且不会对水泥凝结时间和强度产生不良影响。
The results show that composite inhibitors have excellent corrosion inhibition efficiency and won't give bad effect on cement setting time , flexural strength and compressive strength.
本标准规定了水泥标准稠度用水量、凝结时间和由游离氧化钙造成的体积安定性的检验方法。
This standard specified the testing methods of water requirement of normal consistency, setting time as well as soundness of portland cements caused by free calcium oxide.
采用自制的复合缓凝剂配制出脱硫粉刷石膏，并对脱硫粉刷石膏的凝结时间及力学性能进行了研究。
Desulphurization render gypsum can be prepared using composite retarder and some tests study on the setting time and mechanical property of desulphurization render gypsum.
固化磷石膏磨制的水泥和天然二水石膏磨制水泥相比，二者的凝结时间最接近，强度有一定的提高。
Cement prepared with solidified phosphogypsum as retarder had similar setting time as cement prepared with natural gypsum and higher strength than them.
对注浆加固公路路基用的水泥浆体从稳定性、流动度、粘滞度、凝结时间、析水率等方面进行了研究。
In this paper, the behavior of grouting cement mortar to reinforce highway subgrade is analyzed from the aspects of stability, fluidity, viscosity, bleeding ratio and setting time of cement mortar.