一种无填充的低粘稠度环氧树脂胶。
本文叙述了双环氧树脂胶研制，并确定出最佳工艺方法。
In this paper, the principles and method of dual-epoxy resin are discussed, the optimum technological process has been given.
液态聚硫橡胶增韧的环氧树脂胶表现出良好的抗冲击性能和抗弯曲性能；
Epoxy resin toughened by liquid polysulfide rubber exhibits good anti-impact performance and anti-bend performance.
DOVER系列低温固化胶是单组份、低温热固化改良型环氧树脂胶粘剂。
DOVER series low temperature curing adhesives are one part, low temperature heat curable epoxy.
介绍了环氧树脂胶的配制，修补玻璃仪器玻璃仪器的种类、方法及注意事项。
This paper discusses the make-Np and the types of epoxy resin. It also shows us the way and problems to be noted in mending glass instruments with epoxy resin.
BSEN 10289岸上和海上管路钢管及配件加有环氧树脂和改性环氧树脂胶的外用液体。
BS EN 10289 Steel tubes and fittings for onshore and offshore pipelines-External liquid applied epoxy and epoxy-modified coatings.
我曾尝试过用水调成的催化粉胶，也曾尝试过双组份环氧树脂胶、酪蛋白乳胶、胶泥、水胶以及新型超强力胶。
I've tried the two part epoxies, white casein-based glue, contact cement, hydro glue and the new super-glues.
然后，我与他们慷慨涂层超级胶(环氧树脂还要罚款…它只是需要更长的时间)，包括他们蜡纸，并钳制他们使用的一种形式我将木材。
Then I generously coated them with super glue (epoxy would also work fine... it would just take longer), covered them with wax paper, and clamped them in using a form I cut from wood.
灯具使用PVC外壳，隔热、防潮、防腐蚀，经久耐用，采用透明的环氧树脂封胶。
Our LED lights use the PVC casing, which is anti-heat, anti-moisture, anti-corrosion, durable, and use the transparent epoxy glue for sealing.
通过改性环氧树脂及固化剂，实验研究了浸渍胶的粘度、韧性及耐冷热冲击性、浸渍性。
A sort of modified epoxy resin and curing agent in terms of its viscosity, tenacity, cold-proof and heat-proof impinge and dipping properties were described.
对比有胶与无胶纤维布拉伸实验，表明环氧树脂不仅粘接纤维布，对纤维布有保护作用，而且能够显著提高其拉伸强度。
The experiment compare of carbon cloths tension strength with and without glue indicates that the epoxy resin can not only make the fiber adhesive united but also increase the tensile strength.
环氧树脂是聚硫密封胶常用的增粘剂，在聚硫密封胶中加入环氧树脂可以起到明显的增粘作用。
Epoxy resin is the common tackifier for polysulfide sealant. Adding epoxy resin into polysulfide sealant can exert an auxiliary effect on viscosity increasing.
采用环氧树脂-DDS固化体系作为胶接剂，探讨了各种金属表面处理方法、胶接时对胶接面施加的压力、胶层厚度等因素对胶接剪切强度的影响。
The influences of surface treatments, the pressures during bonding process and the thickness of adhesive layer on shearing strength were investigated with epoxy resin-DDS curing system as adhesive.
以甲基丙烯酸甲酯为硬单体，丙烯酸丁酯为软单体，丙烯酸为功能单体，环氧树脂为改性剂制备了密封胶用环氧改性丙烯酸树脂。
The epoxy modified acrylate resin for sealant is prepared with methyl acrylate as hard monomer, butyl acrylate as soft monomers, acrylate acid as functional monomers and epoxy resin as modifier.
以环氧树脂为基体，间苯二胺和氨基二苯甲烷的低融点混合物为固化剂，铜粉为导电填料，制备了热固化各向同性导电胶。
Copper conductive adhesives were prepared using epoxy as matrix, the mixture ofm-phenylenediamine and diaminodiphenylmethane as hardener, and copper particles as the con-ducting filler.
环氧树脂灌封胶在电子电器工业领域应用广泛。
The epoxy resin sealant has extensive application in the electronic and electrical equipment industry.
以环氧树脂为基体，间苯二胺和二氨基二苯甲烷的低融点混合物为固化剂，铜粉为导电填料，制备了热固化各向同性导电胶。
Copper conductive adhesives were prepared using epoxy as matrix, the mixture ofm-phenylenediamine and diaminodiphenylmethane as hardener, and copper particles as the conducting filler.
试验发现，环氧树脂对聚硫密封胶的多项性能都有不同程度的影响。
It was found in this experiment that the epoxy resin had the varying degree influence to the several properties of polysulfide sealant.
使用环氧树脂作为配粉胶比用硅胶寿命短，但初始光通量相对高出25％。
The life of white LED using epoxy resins to mix fluorescent powder is shorter than silica gel, hut initial luminous flux is higher about 25 %.
主要介绍了奇士增韧剂对Y J型环氧树脂浸渍胶的增韧改性。
Toughening of YJ impregnated resin by QS toughened agent is presented.
主要介绍了奇士增韧剂对Y J型环氧树脂浸渍胶的增韧改性。
Toughening of YJ impregnated resin by QS toughened agent is presented.