The recuperator tube of ammonia condenser on a factory was made of 316l stainless steel and pitted after used for only one year.
某公司的立式氨冷凝器波纹换热管采用316L不锈钢制造，使用1年后陆续发生腐蚀穿孔现象。
Analyzes the design defects of ammonia condenser in SNAM ammonia stripping process urea plant and provides the improvement methods.
剖析斯那姆氨汽提法尿素生产装置中氨冷凝器的设计缺陷，提出改进措施。
It was found that the leakage cause of the ammonia condenser tubes was the electrochemical corrosion due to the cooling water based on the analysis on the cooling water, tubes and the scales.
通过对冷却水、传热管以及垢层的分析检验，发现氨冷凝器传热管泄漏是由冷却水对金属的电化学腐蚀引起的。
The ammonia circulates through a condenser and then an evaporator, where it provides the cooling, before being reabsorbed by the water.
氨经冷凝器后流入蒸发器，在这里它在被水再次吸收之前提供制冷效果。
Ammonia corrosion of condenser copper tubes in the air removal section cannot be avoided as a result of ammonia collection and existence under super cooling condition.
由于氨的聚集与氧的存在，在凝汽器空冷区出现过冷度的情况下，铜管的氨腐蚀是不可避免的。
Through the use of highly energy-efficient evaporative condenser, it completes the technological transformation of the refrigeration compressor exhaust cooling system at ammonia cooling system.
通过采用高效节能型蒸发式冷凝器，对氨冷却系统工序中制冷压缩机排气冷却系统进行了技术改造。
The corrosion failure of vertical ammonia-seawater condenser used in acetone-benzol plant was introduced. It is determined that the main failure reason is caused by seawater local corrosion.
介绍了酮苯装置立式氨用冷凝器的失效情况，确定了海水局部腐蚀是冷凝器失效的主要原因。
The corrosion failure of vertical ammonia-seawater condenser used in acetone-benzol plant was introduced. It is determined that the main failure reason is caused by seawater local corrosion.
介绍了酮苯装置立式氨用冷凝器的失效情况，确定了海水局部腐蚀是冷凝器失效的主要原因。