In this paper, the effect of annealing temperature and time on the rate of metal-induced lateral crystallization (m ILC) of amorphous silicon are investigated in detail.
详细研究了金属诱导非晶硅横向晶化时间、温度对晶化生长的影响。
Tbe present paper is devoted to describe the effect of the implanted energy, dose, and annealing temperature and time on electrical characteristics of circuit components.
文中着重介绍了注入离子能量、剂量、退火温度及时间对电路元件电学性能的影响。
The process of annealing consists of heating the steel to an elevated temperature for a definite period of time and, usually, cooling it slowly.
退火工艺的组成为把钢加热到一定温度并保持一段时间,通常再缓慢冷却。
The effects of baking temperature, baking time and prestrain on the bake hardenability and dent resistance of isotropic sheet steel and BH sheet steel produced by batch annealing were studied.
研究了烘烤温度、烘烤时间和预拉伸应变量对罩式炉退火工艺生产的各向同性钢的烘烤硬化性的影响,并与力学性能相当的冷轧烘烤硬化钢进行了对比。
The accurate control of the work pieces temperature in vacuum annealing furnace is a typical nonlinear large time delay and cross coupling complicated problem.
而在真空退火的生产过程中,退火工件温度的精确控制是一个典型的非线性、大时滞、强耦合的复杂控制问题。
The influences of cooling rate after the forge on the heating temperature and time of apheroidized annealing of steel T10 was studied.
研究了锻造后的冷却速度对T10钢等用球化退火加热温度和保温时间的影响。
In addition, both hydrogen permeation time and trapping coefficient of hydrogen increase but the hydrogen diffusivity decreases in the steel with the elevation of annealing temperature.
此外,随着退火温度的提高,氢渗透时间和氢陷阱系数也增大,而氢的扩散系数则降低。
The results indicate that the blue shift of band gap depends on the annealing temperature and annealing time. Choosing reasonable annealing condition can control the magnitude of blue shift.
实验结果表明,带隙蓝移同退火时间和退火温度有关,合理选用退火条件可以控制带隙的蓝移量。
The annealing process was made under different temperature and holding time to the cold forging AZ31 magnesium alloy with different deformation ratio.
对不同变形量的冷锻az31镁合金在不同温度和保温时间下进行退火。
The new temperature updating function derived is inversely proportional to a power function of the annealing time and is independent of the dimension of the optimization problems.
新的温度更新函数与退火时间的幂函数成反比,与优化问题的变量维数无关。
The results show that crystallization behaviors of the BST thin film are strongly dependent on the annealing temperature, the annealing time and the heating rare.
研究结果表明,BST薄膜的晶化行为强烈依赖于退火温度、退火时间和加热速度。
Conductivity was increased with the increase of volume ratio, annealing temperature and annealing time.
随覆层材料体积比的增加、扩散退火温度的升高及扩散退火时间的延长而升高。
The results show that the annealing temperature was reduced, the annealing time was reduced and the mechanical properties were enhanced, which has remarkable energy conservation effect.
结果表明:大大降低退火温度,缩短退火时间,提高力学性能,综合节能效果显著。
The results indicate that the surface quality, FD and resistivity of the film increase with the sputtering time, but decrease with the Annealing temperature.
随着退火温度的上升,薄膜表面质量下降,分形维和电阻率也随之降低。
The residual stress in the specimens was related to the annealing time, and the there was a linear proportion by inversion between the annealing temperature and the interfacial residual stress.
样品的残余应力与退火时间有关。温度与界面残余应力成线性反比关系。
This paper summed up the tensile strength of steel wire, annealing temperature and annealing time by experimental datas of wire annealing.
利用钢丝退火试验数据,总结了钢丝的抗拉强度、退火温度和退火时间的关系。
The results show that, different annealing temperature and holding time have different effects on the shape memory capability and superelasticity of the shape memory alloy wires.
结果表明:不同的退火温度和退火时间对试样的形状记忆性能以及超弹性具有不同程度的影响。
The appropriate sputtering time, sputtering power and annealing temperature are needed for improving the quality of films fabricated by ms.
合适的溅射时间、溅射功率和提高退火温度是改善磁控溅射成膜的关键。
The result shows that: The resistance of films are changed with substrate temperature and annealing conditions (annealing temperature and annealing time).
实验结果表明:通过控制基体温度和退火条件(退火温度及退火时间等)可以改变膜电阻。
A method of annealing for a long time at low temperature can be used to improve the plasticity and make the products acceptable.
提出用低温长时间退火的方法改善其塑性,通过试验确定了退火工艺制度,使产品的变形性能达到了使用要求。
A method of annealing for a long time at low temperature can be used to improve the plasticity and make the products acceptable.
提出用低温长时间退火的方法改善其塑性,通过试验确定了退火工艺制度,使产品的变形性能达到了使用要求。