The reaction process and curing mechanism were basically identical to the curing reaction of bisphenol A epoxy resin with anhydride in the presence of accelerator.
固化反应过程及固化机理与促进剂作用下酸酐固化双酚A型环氧树脂的反应基本相同。
The forming mechanism of hydrolyzable chlorine and its industrial reducing technology have been explored, with bisphenol a epoxy resin, by the author. And an effective way has been found.
本试验以双酚a型环氧树脂为例，对可水解氯的形成机理以及降低其含量的工业化工艺路线作了探索，找到了有效的降氯方法。
Synthesis and properties of Bisphenol-A standard epoxy vinyl ester resin were discussed in this paper.
合成了标准型的环氧乙烯基酯树脂，对其性能进行了表征。
In this article, a novel liquid crystalline epoxy resin was synthesized, and curing behavior and mixed with bisphenol-A epoxy resin were investigated.
本文合成了一种新型液晶环氧树脂，并对其固化及改性普通双酚- A环氧树脂进行了较系统的研究。
A new kind of epoxy resin adduct polyol (EAP) with rigid backbone was synthesized by the reaction of bisphenol - a type epoxy resin with acetic acid and characterized with FTIR and 1h - NMR.
用双酚a型环氧树脂与乙酸反应，合成了具有刚性骨架的环氧树脂加成多元醇(EAP)，并用FTIR与1h - NMR对其进行了表征。
A review is given on the development status of the synthesis techniques of low-molecular-weight epoxy resin of bisphenol a type.
就低分子量双酚a型环氧树脂的合成技术进展状况予以概述。
The encapsulate composite for pulsed piezoelectric power supplier was investigated in this paper, in which a bisphenol A liquid epoxy EP828/E51 was resin matrix and aluminum oxide was filler.
本论文研究的复合封装材料以双酚A型环氧树脂EP828／E51作为基体，以氧化铝作为填充材料，有望替代纯环氧固化物作为脉冲压电电源用新型封装材料。
Vinyl ester resin was synthesized using bisphenol A type epoxy resin and methylacrylic acid as raw materials.
以环氧树脂和丙烯酸为基本原料，合成环氧丙烯酸酯并进行了表征。
As substitutes for Bisphenol a, used for polycarbonate, epoxy resin, polyester, and phenolic resin synthesis, as well as developer for photographic material and thermal paper.
作为双酚a的代用品，可作为聚碳酸酯、环氧树脂、聚酯、酚醛树脂的原料，以及聚砜、聚醚砜的原料。也用于彩色摄影材料和热敏材料显色剂。
Disclosed is a modified liquid epoxy resin having low viscosity and high performance, which is obtained by reacting a mixture of a bisphenol and a phenol aralkyl resin with an epihalohydrin.
本发明提供一种使双酚类和芳烷基酚醛树脂的混合物与环氧卤丙烷反 应得到的低粘度且高性能的变性液性环氧树脂。
The modification effects on diglycidyl ether of bisphenol A(DGEBA, epoxy resin E-44)were studied by impact test, tensile test, bend test and SEM.
通过冲击试验、拉伸试验、弯曲试验和扫描电镜（SEM）观察等方法，研究了星形聚醚环氧树脂对E-44环氧树脂的改性作用；
The modification effects on diglycidyl ether of bisphenol A(DGEBA, epoxy resin E-44)were studied by impact test, tensile test, bend test and SEM.
通过冲击试验、拉伸试验、弯曲试验和扫描电镜（SEM）观察等方法，研究了星形聚醚环氧树脂对E-44环氧树脂的改性作用；