Microstructure of simulated coarse grain heat affected zone (CGHAZ) of Zr Microalloyed HSLA Steel are investigated using optical microscopy and transmission electron microscopy.
采用光学显微镜和透射电镜研究了锆处理对微合金钢粗晶热影响区组织的影响。
The transformation superplasticity in welding CGHAZ (Coarse Grain Heat Affected Zone) of EH36MOD steel and its effect on fatigue life have been studied with thermal simulating method.
采用热模拟方法，对EH36MOD钢焊接热影响区粗晶区(CGHAZ)的相变超塑性及其对疲劳寿命的影响进行了研究。
Owing to heat action during X80 pipeline steel welding the organization and performance of heat affected zone will change considerably in particular of coarse grain heat affected zone (CGHAZ).
X80管线钢在焊接过程中，热影响区由于受到焊接过程热的作用，其组织和性能会发生较大的变化，尤其是粗晶热影响区的组织和性能变化最大。
The fracture rod has cracks in the microstructure of weld zone, intergranular cracks exists in the coarse grain zone of the weld heat affected zone.
进一步比较了断裂拉杆和已经产生裂纹的拉杆焊缝区的显微组织，发现在焊缝的热影响区粗晶区存在沿晶裂纹。
In welding test of TCS stainless steel, it was found that impact absorbing energy of heat-affected zone (HAZ) near bond line in welded joint was low. The reason is coarse grain in HAZ.
在TCS不锈钢前期焊接试验中发现其焊接接头热影响区的冲击吸收功值在熔合线附近较低，原因是接头热影响区晶粒粗大所致。
In welding test of TCS stainless steel, it was found that impact absorbing energy of heat-affected zone (HAZ) near bond line in welded joint was low. The reason is coarse grain in HAZ.
在TCS不锈钢前期焊接试验中发现其焊接接头热影响区的冲击吸收功值在熔合线附近较低，原因是接头热影响区晶粒粗大所致。