The author proposed the principle to select the curing temperature and functional relations of the viscosity with curing temperature and time for three different resin systems.
提出了选择固化温度的原则，以及三种不同树脂固化体系粘度随固化温度、固化时间变化的函数关系。
On the basis of experiments and analysing the effects of the constant temperature and curing time on the strength of fly-ash, the best curing temperature and time are obtained.
在实验的基础上通过对恒温温度及养护时间对粉煤灰强度影响的分析，得出粉煤灰制品的最佳养护温度和时间。
The effects of type, concentration of chain extender, curing temperature and time of silicone sealants with low modulus and high elongation on their mechanical properties were studied.
制备了不同低模量高延伸率室温硫化有机硅密封材料，并考察了扩链剂类型和用量、固化温度和时间对材料性能和交联度的影响。
Viscosity of the RFI resin film as a function of curing temperature and time were tested respectively. The mechanical properties of stitched and unstitched composite laminates were evaluated.
测试了改性环氧树脂胶膜熔体粘度对固化温度和时间的依赖性，将缝合与未缝合复合材料层合板试样的基本力学性能进行了试验对比。
The interval of the coating time is determined by the temperature at the time of construction and the degree of curing of the film (by hand).
重涂时间的间隔，由施工时的温度和涂膜固化的程度（以手触不粘）来确定。
The optimum post curing conditions of fluororubber blends were determined by changing the temperature and the time.
通过改变不同配方的氟橡胶二段硫化温度和时间，确定了最佳硫化条件。
The gelation time of this epoxy resin with modified liquid anhydride was related to the chemical structure and the composition of epoxy resin, curing temperature and accelerator.
环氧树脂与改性液体酸酐体系的凝胶时间与环氧树脂的结构与组成、固化温度及促进剂等因素有关；
As for curing process, the influence of dosage of curing agent and curing temperature on gel time was investigated.
在固化工艺方面，研究了固化剂含量和固化温度对于凝胶时间的影响。
The effects of high temperature, standing time after cooling, methods of cooling and curing on the compressive strength of concrete are discussed.
探讨了受火温度、高温后静置时间及冷却和养护方式对火灾高温后混凝土抗压强度的影响。
Many factors impacting on its bonding reliability and the optimum parameters of bonding were studied, such as bonding temperature, curing time, bonding pressure, conductive particles fraction.
介绍各向异性导电胶导电机理和粘接工艺，以及影响它的粘接可靠性因素和最佳参数的研究，如粘接温度、固化时间、粘接压力、粒子含量等。
The effects of PPC content, curing agent, curing temperature, curing time and adding carbon black on the mechanical properties of the blends were studied.
研究了PPC的添加量、硫化剂的种类及用量、硫化时间、硫化温度和添加炭黑对共混弹性体的物理力学性能、交联度的影响。
Effect of curing temperature, curing time, resistance to media, kind and volume of the sand-laden fluid, and particle size of proppant on fibre compound sand control system were discussed.
探讨了固化温度、固化时间、耐介质性、携砂液的种类和用量以及支撑剂粒径等对纤维复合防砂体的影响。
Effects of process conditions such as different curing temperature, curing time, starting reaction temperature and casting flaw on polyurethane elastomers mechanical properties are investigated.
研究了工艺条件(不同固化温度、固化时间和初始反应温度)以及浇注成型产生的缺陷对聚氨酯弹性体力学性能的影响。
The results showed that the increasing of curing temperature could improve the compressive strength and shorten the curing time of fly ash based mineral polymer.
结果表明：提高养护温度可以提高粉煤灰基矿物聚合物的抗压强度，缩短养护时间。
The effects of curing time, temperature and bleeding capacity on ice-formation pressure of grout were studied.
研究了养护温度、时间及泌水率对灌浆材料结冰压的影响。
Overview AJD-I Automatic Temperature Curing time is the struggle against traditional scald the lack of fetal development and production of premium.
概况ajd - I型自动定时温控硫化机是针对传统电烫斗补胎的不足而研制生产的。
Aiming at the market demands, post curing process of cotton fabric was carried out, the influences, of selections of resin and the catalyst, curing conditions of temperature and time were analyzed.
根据市场要求，对棉织物后焙烘加工工艺，包括树脂和催化剂的选择，整烫和焙烘条件(整烫温度、蒸汽湿度等)等方面进行工艺分析。
Then, it makes target mixture proportion design to study on the aggregate gradation scope, optimum asphalt content of mixture, the temperature and time of curing.
然后，对确定配合比例的国产环氧沥青进行混合料目标配合比设计，确定了矿料的级配范围、混合料的最佳油石比以及高温固化温度、时间等参数。
Test shows that the curing temperature and curing time are the main factor which affect the whiteness fading and color change of printed white garment.
结果表明，白布在经后整理及成衣印花后，白度下降及颜色变化主要是由后整理及印花中的高温处理温度及时间引起的。
Through analyzing each factor such as concentration of citric acid and chitin, curing temperature as well as curing time, the optimum condition is defined for the anti-crease finish.
对柠檬酸、壳聚糖及焙烘温度和焙烘时间等进行了单因素分析，确定了防皱整理的最佳工艺。
A study was made on concrete creep under different curing temperatures, and the comprehensive effects of time and temperature on creep development were expressed with the chemical reaction rate.
对不同养护温度下的混凝土徐变进行了研究，用化学反应速率描述温度对混凝土徐变的影响。
Automatic pressure compensation, adjust the time and deflated deflated the number of heating temperature, curing time.
可自动压力补偿、调节放气时间和放气次数、加热温度、硫化时间等。
Then, it makes target mixture proportion design to study on the aggregate scope, optimum asphalt content of mixture, the temperature and time of curing.
进行了环氧沥青混合料目标配合比设计，确定了矿料的级配范围、混合料的最佳油石比以及高温固化温度、时间等参数。
Research progress in influencing factors of properties of nano-filler ECAs, such as content, size, shape, surface state of nano-fillers, curing temperature and curing time etc, was reviewed.
从纳米填料含量、粒径、形状与维度、表面状态、固化温度与固化时间等方面综述了纳米填料导电胶性能影响因素的国内外研究进展；
The effect of variations in kinds and concentrations of catalysts, resin concentrations, curing-temperature and-time on the wrinkle recovery and tensile strength is given.
本文中报告了关于催化剂种类和用量、树脂浓度、焙烘温度和时间的变化对织物的防皱性及强力的影响。
The real time monitoring for residual strain induced by resin cure during the RTM process was realized by measuring the relationship among wave deflection, temperature and curing time.
通过光纤光栅波长偏移与温度和固化时间之间的关系测试，得到了树脂固化过程中残余应变的变化历程，成功实现了RTM工艺树脂固化过程中残余应变的在线监测。
In order to shorten test time, a forced drying method is adopted in preparing sample so as to measure gloss and colour of self-curing paint film at ambient temperature.
为缩短检验时间，采用强制干燥方法制备样板，对需要常温自干漆膜的光泽和色泽进行测定。
The amount of plasticizer, film thickness, curing temperature and curing time effect the release of the DS from the tablet coated with ethylcellulose aqueous dispersion.
结论 ：乙基纤维素水性分散体可作为缓释衣膜材料。增塑剂用量、衣膜厚度、后处理温度、后处理时间等因素均影响药物的释放。
It can be quicky cured and resisted high temperature for class H in a short curing time and low evaporation losses.
它耐高温达到H级，固化速度快，贮存周期长，挥发率低。
It can be quicky cured and resisted high temperature for class H in a short curing time and low evaporation losses.
它耐高温达到H级，固化速度快，贮存周期长，挥发率低。