After rapid thermal annealing(RTA) in Ar atmosphera at high temperature, the flow pattern defects(FPDs) density decreased more sharply in Sb-doped wafers than that in lightly B-doped wafers.
研究了掺杂剂原子种类及快速热处理技术对大直径直拉硅单晶中空洞型微缺陷密度的影响。
After rapid thermal annealing(RTA) in Ar atmosphera at high temperature, the flow pattern defects(FPDs) density decreased more sharply in Sb-doped wafers than that in lightly B-doped wafers.
研究了掺杂剂原子种类及快速热处理技术对大直径直拉硅单晶中空洞型微缺陷密度的影响。