Liquidus temperature of actual aluminum electrolyte samples was measured directly.
直接测定了铝电解质实际样品的初晶温度。
The adiabatic heating induces the temperature of fracture surface layer to be higher than the liquidus temperature too.
计算表明，断口表面层绝热升温温度依然高于液相线温度。
Low liquidus temperature enables low bath temperature. The current efficiency increases with the decreasing of bath temperature.
低液相线温度允许低电解温度，而降低电解温度可大大提高电流效率。
Influence factors, such as liquidus temperature, superheat degree, electrolyte components, and the depth of molten salt were focused.
主要研究了初晶温度、过热度、电解质组成，以及电解质融化之后的熔盐深度对铝溶解度的影响。
The DSC results indicate that above the liquidus temperature, the ZL114A alloy melts structure varies with the increase of temperature.
综合热分析dsc结果表明：在液相线以上，ZL114 A合金熔体的结构状态随温度发生变化。
With the steel line and the solid phase of the high and low liquidus temperature and crystallization temperature of the size of interval.
它们与钢的固相线和液相线温度的高低及结晶温度区间的大小有关。
Solidus and liquidus temperatures of the rocks and relationship between crystallinity and crystallization temperature have been determined.
确定了岩石固相线与液相线的温度，岩石结晶程度与温度的关系。
Besides the cell voltage, bath temperature and bath ratio, the inputs of the system also include the liquidus temperature, superheat extent and cathode voltage.
系统的输入参数除传统的电压、温度和分子比外，还采用初晶温度、过热度和阴极压降等作为系统的输入参数。
Metal is preheated in a furnace or crucible until is above the liquidus temperature in a suitable range (we don't want the metal solidifying before the pour is complete).
金属在熔炉或坩埚中预热到高于液化温度的一个合适范围内(不希望金属在浇铸完成前凝固)。
During the melting and processing practices, an accurate knowledge of liquidus temperature is necessary in the determination of process parameters relating to a given alloy.
在合金熔炼和加工过程中，往往需要知道液相线温度，以便确定相关工艺参数。
The compositions can be designed using theoretical calculations of the liquidus temperature to have substantial amounts of refractory metals, while still maintaining a depressed liquidus temperature.
所述组成可以使用液相线温度的理论计算进行设计以便包含大量的难熔金属，并仍然保持低的液相线温度。
The results show that: manganese lowers liquidus and eutectic temperature, and narrows down the temperature range of solidification;
结果表明：锰降低液相线温度和共晶温度，缩小凝固温度范围；
In the liquidus nearby, the grains size becomes coarse with increasing of casting temperature.
在液相线附近，晶粒尺寸随着浇铸温度的降低而逐渐减小并呈球化的趋势。
In recent years, it has been shown that many binary alloy melts experience temperature-induced discontinuous liquid-liquid (L-L) structure transition hundreds degrees above the liquidus.
近年来研究发现，很多二元合金在熔点以上一定温度范围内发生温度诱导非连续液-液结构转变。
The engendering rule of organism of liquidus casting aluminum alloy A356 at different heat preservation temperature, different heat preservation time was investigated.
研究了液相线铸造A35 6铝合金在不同保温温度、不同保温时间下的组织形成规律。
In recent years, it has been found that many alloys' melt experienced temperature-induced discontinuous L-L structure transition at a certain temperature above liquidus.
近年来的研究不断发现，很多合金熔体在熔点以上一定温度范围内会发生温度诱导的非连续液-液结构转变。
The bath temperature, liquidus and anode effect were controlled by adjusting the AlF3 additions, aluminum tapping magnitude, cell voltage set-point and the alumina feeding interval.
通过调整氟化铝添加量、出铝量和设定电压，以及氧化铝下料间隔的自修正，实现对电解槽温度、初晶温度、效应系数的控制。
The bath temperature, liquidus and anode effect were controlled by adjusting the AlF3 additions, aluminum tapping magnitude, cell voltage set-point and the alumina feeding interval.
通过调整氟化铝添加量、出铝量和设定电压，以及氧化铝下料间隔的自修正，实现对电解槽温度、初晶温度、效应系数的控制。