The lower sintering temperatures and shorter sintering time are used in the sintering process for fine molybdenum powder sintering characteristics of low-temperature activation.
由于超细钼粉低温活化烧结特性，在烧结过程中降低烧结温度，减少烧结时间，有效地提高钼板坯的晶粒数，同时降低了车间的生产成本。
As substitution of diopside for talc, the body has lower firing temperature and widening sintering range. The property of diopside porcelain is in keeping with standard of high frequence dielectric.
用透辉石代替滑石时，透辉石瓷有较低的烧成温度和较宽的烧结范围，其性能符合高频电介质标准的要求。
Lead scandium tantalate ceramics exhibit excellent dielectric, piezoelectric, and ferroelectric properties, but need rather higher sintering temperature and possess lower Curie temperature.
钽钪酸铅陶瓷具有优良的介电、压电和铁电性能，但烧成温度高、居里点较低。
The results show that the lower the sintering temperature, the lower the bulk density.
结果表明，烧结温度过低，试样的致密度差；
In addition, the sintering material with a small diameter corresponds to a lower minimum sintering temperature.
研究同时发现，颗粒物料的粒径减小，流化颗粒的最小粘结温度减小。
To lower temperature sintering is desired for the fabrication of multiplayer microwave ceramics.
为满足多层微波元件低温烧结的需求，必须降低微波介质陶瓷的烧结温度。
Powder bed temperature of sintering process should be lower than agglomeration temperature of composite wax powder, which result in dimensional instability.
为了使蜡模获得稳定的尺寸，烧结过程中的粉床温度应尽量低于蜡粉材料的板结温度。
The results suggest that the KOH can lower down the synthesized temperature by 300 K, and the as-synthesized powder smaller and easier to densify in the sintering process.
结果表明：室温KOH 的处理，相比高温固相合成工艺降低了合成温度300K。合成粉体颗粒更为细小，具有优良的成型和烧结性能。
The results suggest that the KOH can lower down the synthesized temperature by 300 K, and the as-synthesized powder smaller and easier to densify in the sintering process.
结果表明：室温KOH 的处理，相比高温固相合成工艺降低了合成温度300K。合成粉体颗粒更为细小，具有优良的成型和烧结性能。